Efficiency of protective coatings on high creep resistant cast steel
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2
Abstract
This paper presents results of research of multilayer aluminium–silicon coatings. Aluminium–silicon coatings were created on high– temperature creep resist cast iron using slurry method in air atmosphere. These coatings protect equipment against hot corrosion in carburizing atmosphere at thermal shocks conditions. Various technological parameters of coatings manufacturing were applied. Main technological parameters were: temperature and time of annealing and Al-Si ratio in the active mixture. The structure of obtained coatings is three-zonal. Phase composition of two external zones ensures protection against carburizing, but these zones are not resistant to cracking. The cracks form as a result of thermal shocks. The internal zone of the coatings situated next to substrate compensates for differences of thermal expansion of the coating and the substrate. The cracks are stopped in the internal zone and do not propagate into the substrate material. Protective efficiency of the coatings at carburizing conditions with thermal shocks was determined. Structure of the coatings before and after carburizing and thermal shocks is described in present paper. Thickness, chemical composition (EDS) and phase composition (XRD) of the coatings are determined. Correlation between the coatings structure and depth of carburized layer was determined.
Authors and Affiliations
A. Kochmańska, J. Kubicki
Keywords
Related Articles
- EP ID EP70558
- DOI -
- Views 67
- Downloads 0
Application of time-series analysis in foundry production
Characterization of the time-series analysis is presented, as a data mining tool which facilitates better understanding nature of manufacturing process and permits forecasting of future values of the process parameters o...
Analysis of the applicability of domain ontology in copper alloys processing
Efficient use of corporate resources in the form of intellectual capital is due in large measure to effectiveness of knowledge codification and distribution systems. Making intellectual resources available to employees i...
Development of the fundamentals of melting and casting technology of Al-Me (Cr, Ni, Mo, W, Ti) master alloys used for modification of microstructure in silumins
The study presents the technological backgrounds of the process of melting and casting Al-Cr, Al-Ni, Al-Mo, Al-W and Al-Ti master alloys, used as refiners of the microstructure of cast silumins. Basing on the analysis of...
Selected characteristic of silumins with additives of Ni, Cu, Cr, Mo, W and V
The study, presents an investigation results of new grades of silumins containing of: 7,0÷17,0% Si, 4,0% Ni, 4,0% Cu and 0,5% Cr, Mo, W each as well as V. The influence tests were carried out of - antimony addition, stro...
Evolution of Mg-5Al-0.4Mn microstructure after rare earth elements addition
Mg-5Al-0.4Mn-xRE (x = 0, 1, 2, 3 wt.%) magnesium alloys were prepared successfully by casting method. The microstructure was investigated by light microscopy. The influence of rare earth (RE) elements on the area fractio...