EVALUATION OF MICROSTRUCTURAL STABILITY OF DISSIMILAR WELD JOINTS
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2011, Vol 18, Issue 4
Abstract
The microstructural changes occurring in the weld joint P92/316Ti during his long-term exposure at high temperature were studied. In parallel to experiments were carried out calculations of phase equilibria for the base materials and the weld joint using the ThermoCalc software. Based on the experimental results and computational modeling results were evaluated a microstructural stability and the application of the base materials and the weld joint.
Authors and Affiliations
Pavel Sohaj
Keywords
Related Articles
- EP ID EP155526
- DOI -
- Views 110
- Downloads 0
Fatigue Crack Propagation Under Variable Amplitude Loading Analyses Based on Plastic Energy Approach
Plasticity effects at the crack tip had been recognized as “motor” of crack propagation, the growth of cracks is related to the existence of a crack tip plastic zone, whose formation and intensification is accompan...
PRELIMINARY RESULTS IN SYNCHROTRON X-RAY DIFFRACTION MEASUREMENTS OF RUBBER COMPOSITES STRUCTURE BEFORE AND AFTER EXPOSURE TO HYDROGEN
In future years, fuel cells are expected to represent a promising technology as a source of heat and electricity in buildings and of electrical power for vehicles, since fossil fuels are exhausting and significantly degr...
The investigation of the corrosion resistance of the tension clamps Skl14
At the level crossings it is possible to find the problems with the corrosion of the parts of the fastening system. These problems are especially at the rubber level crossings and in the tunnels. As a part of the thesis...
CYCLIC PLASTIC BEHAVIOUR OF UFG COPPER UNDER CONTROLLED STRESS AND STRAIN LOADING
The influence of stress- and strain-controlled loading on microstructure and cyclic plastic behaviour of ultrafine-grained copper prepared by equal channel angular pressing was examined. The stability of microstructure i...
34CrMo4 steel resistance against the SSC after controlled cooling process
The sulphide stress cracking corrosion resistance of 34CrMo4 steel after the accelerated cooling process under the Ar3 temperature was investigated. Two modes of heat treatment were applied to achieve homogeneous microst...