Features of Time Characteristics of Diffusion Properties of Polymer Modified Film Materials for Technical Application
Journal Title: Фізика і хімія твердого тіла - Year 2018, Vol 19, Issue 1
Abstract
The changes of the oxygen permeability of packings from polymeric film materials intended for prolonged storage of metal products have been investigated. High indexes of initial oxygen permeability were recorded due to insecure insulating properties of weld seams, as well as increased diffusion characteristics after the third year of exploitation, The most characteristic structural defects, which emerging in polyethylene modified materials during the period of prolonged storage , have been identified by means of electron microscopic studies.
Authors and Affiliations
N. I. Domantsevych, B. P. Yatsyshyn, M. N. Kril’
Keywords
Related Articles
- EP ID EP328241
- DOI 10.15330/pcss.19.1.95-99
- Views 68
- Downloads 0
The Influence of Physical Fields on the Thermal or Dielectric Properties of Epoxy Composites
The latest developments in the field of materials to improve the physical and chemical properties is the use of physical modification of polymeric materials. The specimens of polyepoxy and composites on the base metal ox...
Influence of Doping and Two-temperature Annealing on CdTe:Br Defective Subsystem
The influence of impurities and annealing conditions on the electrical properties of single cadmium telluride crystals with bromine doping grown by Bridgman method and annealed in cadmium atmosphere at temperatures T = 8...
Improvement of Sorption Parameters of Nickel Ions on Bentonite in the Result of its Irradiation by Microwaves
The adsorption isotherms of nickel ions from aqueous solutions on bentonite, a natural argillaceous material, previously prepared using ultrahigh-frequency electromagnetic waves ("microwaves") were researched in the arti...
The Influence of Step-By-Step Air Exposition of the Zr-Mn-Cr-Ni-V Alloy on Cycle Life
In the course of the research it was determined that step-by-step air exposition of the Zr-Mn-Cr-Ni-V alloy (in the form of ingot and powder) facilitating the formation of concentration inhomogeneity significantly increa...
Features of Structural, Energy and Kinetic Characteristics of Hf1-xErxNiSn Solid Solution
The features of structural, energy state and electrokinetic characteristics were investigated for Hf1-xErxNiSn solid solution in the range: T = 80 – 400 K, x = 0 - 0.10. It was confirmed partly disorder crystal structure...