Fracture Analysis and Rectification of Trunk Lid Torsion Bar Spring

Journal Title: Automobile Technology & Material - Year 2024, Vol 39, Issue 3

Abstract

In order to determine the fracture mechanism and cause of the trunk lid torsion bar spring, the fracture morphology, composition, size, material strength, microstructure and residual stress were tested, and a comprehensive analysis was conducted in combination with background information. The results indicate that the torsion bar spring of the trunk lid experienced high-strength steel delayed cracking at the concentrated bending stress caused by high material strength, insufficient tempering, and high residual stress. Based on the cause of cracking, improvements were made from two aspects: controlling the strength of raw materials and optimizing the stress relief tempering process to reduce residual stress, and ultimately the delayed cracking failure of the luggage torsion bar spring was effectively solved.

Authors and Affiliations

Min Liang

Keywords

Related Articles

Analysis and Optimization of Welding Deformation on Vehicle Exhaust Pipe Flange

When the exhaust pipe is welded with the flange, the welding deformation of the flange affects the tightness of the exhaust pipe assembly. In order to avoid excessive welding deformation of flange during manufacturing,th...

Fracture Analysis and Rectification of Trunk Lid Torsion Bar Spring

In order to determine the fracture mechanism and cause of the trunk lid torsion bar spring, the fracture morphology, composition, size, material strength, microstructure and residual stress were tested, and a comprehen...

Research on the Fasten Process of Coupler Based on Automatic Spindle Equipment

In order to improve working efficiency, operation accuracy and safety, and reduce the error rate, based on the automatic spindle equipment, after the engine is connected to the gearbox, the servo motor of the spindle e...

Study on Fracture Failure Behavior of 6082 Automotive Aluminum Alloy Profile

Based on the Gissmo damage failure model, the failure parameters of 6082 automotive aluminum alloy profile were obtained by numerical parameter inverse method. The reasonability of the Gissmo damage failure model of 608...

Cause Analysis and Solution of LASD Robot Nozzle Block

To address the interference of liquid apply sound deadener (LASD) robot nozzle block on parts installation in the assembly shop, this article analyzed LASD robot nozzle block. Through studying the LASD robot nozzle blo...

Download PDF file
  • EP ID EP732990
  • DOI 10.19710/J.cnki.1003-8817.20220233
  • Views 34
  • Downloads 0

How To Cite

Min Liang (2024). Fracture Analysis and Rectification of Trunk Lid Torsion Bar Spring. Automobile Technology & Material, 39(3), -. https://europub.co.uk/articles/-A-732990