Fusible Models used to Casting Small Dimensions Sculptures
Journal Title: Analele Universitatii "Dunarea de Jos" din Galati. Fascicula IX, Metalurgie si Stiinta Materialelor - Year 2018, Vol 41, Issue 2
Abstract
During the study regarding the obtaining of artworks using light fusible models it has been highlighted the possibility of dividing the process of castingmolding in simple, separate operations, whose execution becomes accessible even to people with no high qualification in the field. An important realization during the study is represented using the dental molding- packaging mass, which has ensured the obtaining of the smoothness of the surfaces and the clarity of form’s configurations. Designing the casting network has been the main preoccupation, in order to ensure the complete action of emptying the wax from the mould and filling it correctly with metal. A special attention has been granted to cleaning and finishing the surface of the sculpture, this operation ensuring the texture of the future artwork.
Authors and Affiliations
Bogdan MURARIU, Beatrice TUDOR
Keywords
Related Articles
- EP ID EP597752
- DOI -
- Views 66
- Downloads 0
Development of Blade Design for Small Hawt Adapted for Lower Values of Wind Speed
The paper aims at studing, theoretically and experimentally, the influence of turbines blade profile on output power, in order to decrease effective domain to smaller wind speed, specific to Galati area. Studies have bee...
The Properties of Hardened Lead
Lead hardened through oxide scattering is investigated as raw materials for the fabrication of the support gratings of lead accumulators in order to increase their life service. For the preparation of lead powder hardene...
Alumina Influence on the Corrosion Resistance of Composite Layers Ni-P-Al2O3
This paper aims to analyze the corrosion resistance of composite layers based on Ni-P matrix and disperse phase alumina of 10 µm size, present in amounts of 5, 10 and 20 g / L in the nickel plating bath. The influence of...
Determination of Friction Coefficient at Sliding Indentation of Laser Cladding with Ni – Cr – B – Fe – Al Alloy
To increase resistance to wear of the surface layers made from 0.45% C steel, a multilayer deposit by powder injection with the chemical composition Cr 8.9%, 4.5% Fe, 5.1% B, 2, 4% Al, 0.6% Cu, and Ni was tested in a mol...
Analysis of Titanium Interface and Tungsten Exterior Layer Thickness Coated by Vibrator Electrode Method
The goal of this paper is to create metallic materials with superior functional performances. The layer obtained by electrode vibrator method must have a very good adherence on part surface and a high chemical and therma...