Influence of Technological Parameters on the Evolution of Nickel Films Deposited by Electrolysis
Journal Title: Analele Universitatii "Dunarea de Jos" din Galati. Fascicula IX, Metalurgie si Stiinta Materialelor - Year 2009, Vol 32, Issue 1
Abstract
The influence of technological parameters on the structure of nickel layers electrodeposited on a copper substrate in a Watts bath has been studied. The complex influence of current densities, temperature and pH values on the formation of the deposition layers are compared. The surface morphology of the nickel films was analyzed by scanning electron microscopy (SEM) and atomic force microscopy (AFM). X-ray diffraction (XRD) was used to investigate the crystallinity of the prepared samples. The increase in the current density leads to fine crystallized films, while layers obtained at even higher current density have dendritic structures. The temperature increasing results in a structure change from fine to coarse.
Authors and Affiliations
Maria POROCH–SERIŢAN, Gheorghe GUTT, Traian SEVERIN, Silviu STROE, Carmen MIHOC
Keywords
Related Articles
- EP ID EP658877
- DOI -
- Views 72
- Downloads 0
Structural Characteristics in Cobalt Based Alloys
In the present paper there are presented results of investigations on samples of partially removable denture made of cobalt base alloys (Co-Cr-Mo) regarding specific structural analysis: determination of structural phase...
Aspects of Nitrated Layer Structure for Some Types of Austenite Stainless Steel
The analysis of nitrated layer diffractograms and the structure marked out the presence of complex nitrides combinations layer for all types of steel except for code 6 steel type 2CuMoNiCr200 which because of the very hi...
Study for Evaluation and Optimization of Mineral Composition and Structure of Iron Ore Granulation in Sintering Process
The characterization of iron ore particles is of vital importance for the study of mineral composition. The specific surface area of iron ore particles can be measured by laser diffraction, and mathematical models (based...
Increase of BOF Converter Life by Own Slag Coating
This paper presents a method for the improvement of the lining life of the BOF converter by slag coating, under nitrogen pressure. Own slag coating of converter lining is put in practice after steel tapping. Dolomite blo...
X-Ray Diffraction Analysis at Ultrasonic Welding
In the article [2] the author present experimental investigations regarding of residual stress distribution in weld bead vicinity of submerged arc welded naval plates. In this way, residual stresses from vicinity of weld...