LABORATORY INVESTIGATIONS OF WEAR RESISTANCE UNDER FRICTION OF A SURFACE LAYER OF 41CrAlMo7 STEEL AFTER GLOW DISCHARGE NITRIDING AS WELL AS ABLATION LASER TEXTURING

Journal Title: Tribologia - Year 2013, Vol 249, Issue 3

Abstract

The paper presents the results of laboratory investigations including measurements of selected parameters in the node of friction (temperature, friction force, wear resistance) with the use of the measured line method for the surface layer of samples steel 41CrAlMo7 after nitriding and laser texturing in combination with cast iron samples. Surface layers after glow discharge nitriding steel were modified using ablative laser micromachining to change its macro- and micro-geometry. In the manufacture regular shaped oil micro-channels and spherical microparticles, we used a Nd: YAG laser with a special focusing system. Comparative research has been subjected to the steel surface topography formed by conventional machining and plasma nitriding and modified after nitriding and laser ablation micromachining. The laboratory tribological investigation used the "pin on disc" method based on a T-11 tribometer. The best results of increasing wear resistance under friction was obtained for the association sample made of steel 41CrAlMo7 after glow discharge nitriding and ablative laser texturing in the geometric arrangement mico-oil containers (micro spherical cap) with a degree of covering of about 25% worked with cast iron anti-samples.

Authors and Affiliations

Wojciech Napadłek, Czesław Pakowski, Adam Woźniak

Keywords

Related Articles

DETERMINATION OF THE ABRASIVE WEAR RATE FOR THE LOW FRICTION COATINGS USING BALL-CRATERING METHOD

In this paper, a micro-scale abrasive wear tests was used to calculate of the abrasive wear rate Kc for the coatings TiN, WC/C and MoS2/Ti. SiC particles, with a mean size diameter of 4 μm, were mixed with distilled wate...

THE INFLUENCE OF MACHINING PARAMETERS ON THE PLACE OF FORMATION AND INTENSITY OF THE WEAR PROCESS OF DRILLS

To determine the wear of drills during their operation, at constant cutting parameters during the one approved tool life under the cut, a series of durability tests of drills made of HS2-5-1 were carried out. The study w...

ANALYSIS OF THE STRUCTURE AND TRIBOLOGICAL PROPERTIES OF SINTERED STAINLESS STEELS

Increasing development of civilization encourages the search for modern engineering materials. At present, very interesting and promising materials are sintered stainless steels that are considered to be the most rapidly...

Badania tribologiczne powłok ceramicznych natryskiwanych plazmowo

Części współczesnych maszyn często wymagają ochrony powierzchni roboczych przed działaniem korozyjnym, zużyciem oraz doraźnymi uszkodzeniami mechanicznymi. Do tego wykorzystuje się powłoki nanoszone na powierzchnie roboc...

PROPERTY ASSESSMENT LUBRICANTS AND TRIBOLOGICAL LOTOS DYNAMIC ENGINE OIL

This paper presents results of research the lubricating properties of welding load Pz, wear under load Ih, the non-scuffing load Pn. scuffing load Pt, and limiting wear load Goz on the tested trade lubricant and modified...

Download PDF file
  • EP ID EP270337
  • DOI -
  • Views 53
  • Downloads 0

How To Cite

Wojciech Napadłek, Czesław Pakowski, Adam Woźniak (2013). LABORATORY INVESTIGATIONS OF WEAR RESISTANCE UNDER FRICTION OF A SURFACE LAYER OF 41CrAlMo7 STEEL AFTER GLOW DISCHARGE NITRIDING AS WELL AS ABLATION LASER TEXTURING. Tribologia, 249(3), 81-96. https://europub.co.uk/articles/-A-270337