Development of in-situ fatigue crack observing system for rotating bending fatigue testing machine
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 35
Abstract
To substitute for a traditional replication technique, an in-situ fatigue crack observing system for rotating bending testing machine has been newly developed. For verifying performance of this observing system, fatigue tests were carried out by using fatigue specimen having a small artificial defect. It is proved that this system can be detect a small fatigue crack and its propagation behavior.
Authors and Affiliations
B. Lian, A. Ueno, T. Iwashita
Keywords
Related Articles
- EP ID EP138480
- DOI 10.3221/IGF-ESIS.35.44
- Views 56
- Downloads 0
Multiaxial fatigue of in-service aluminium longerons for helicopter rotor-blades
Fatigue cracking of longerons manufactured from Al-alloy AVT-1 for helicopter in-service rotorblades was considered and crack growth period and equivalent of tensile stress for different blade sections were e...
Effect of nonlinearity of restrainer and supports on the elasto-plastic seismic response of continuous girder bridge
During an earthquake, the nonlinearity of the bridge structure mainly occurs at the supports, bridge piers and restrainers. When entering nonlinear stage, members of the bridge structure affect the elasto-plastic...
In situ 3D characterization of fatigue cracks displacement fields
The three dimensional growth of fatigue cracks in samples of nodular graphite cast iron is characterized using laboratory X-ray computed tomography. The cracks grow from laser machined artificial defects, their dev...
Evaluation of the material’s damage in gas turbine rotors by instrumented spherical indentation
Experimental indentations are carried out on items of two different materials, taken in several location of various components from high pressure gas turbine rotor which have seen an extensive service. The compon...
The healing of damage after the plastic deformation of metals
The general regularities of damage healing during the annealing after cold deformation of metal materials are presented in this paper. In categories of damage mechanics the kinetic equations of damage healing durin...