Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSW
Journal Title: Frattura ed Integrità Strutturale - Year 2013, Vol 7, Issue 24
Abstract
The effect of processing parameters on the mechanical and metallurgical properties of dissimilar joints of AA6082–AA6061 produced by friction stir welding was analysed in this study. Different FSW samples were produced by varying the welding speeds of the tool as 50 and 62 mm/min and by varying the alloy positioned on the advancing side of the tool. In all the experiments the rotating speed is fixed at 1600rpm. All the welds were produced perpendicularly to the rolling direction for both the alloys. Microhardness (HV) and tensile tests performed at room temperature were used to evaluate the mechanical properties of the joints. In order to analyse the microstructural evolution of the material, the weld’s cross-sections were observed optically and SEM observations were made of the fracture surfaces. The corrosion tests of base alloy and welded joints were carried out in 3.5%NaCl solution at a room temperature. Corrosion current and potential were determined using potentiostatic polarization measurements. It was found that the corrosion rates of welded joints were higher than that of base alloy.
Authors and Affiliations
H. S. Patil, S. N. Soman
Keywords
Related Articles
- EP ID EP114778
- DOI 10.3221/IGF-ESIS.24.16
- Views 54
- Downloads 0
Sn and Ti influences on intermetallic phases damage in hot dip galvanizing
Protection against metallic materials corrosion is one of the most important means to reduce both maintenance costs and environmental impact. In the last years new studies on chemical baths compositions and fluxes...
Fractography as a tool to assess the occurrence of fatigue fractures in complex microstructure structural components
Fractographic assessment of fatigue fractures may be difficult if they occur in metallic components characterized by low ductility complex microstructures. In these cases reconciliation of known fatigue ruptu...
Surface crack growth subject to bending and biaxial tension-compression
Fatigue surface crack growth and the in-plane and out-of-plane constraint effects are studied through experiments and computations for aluminium alloy D16T. Subjects for studies are cruciform specimens under...
A study of the stored energy in titanium under deformation and failure using infrared data
The work is devoted to the experimental study of heat dissipation caused by plastic deformation and failure processes taking place in a titanium alloy Ti-4.2Al-1.6Mn. To investigate the spatial and time evolution o...
Crack initiation and propagation on the polymeric material ABS (Acrylonitrile Butadiene Styrene), under ultrasonic fatigue testing
Crack initiation and propagation have been investigated on the polymeric material ABS (Acrylonitrile Butadiene Styrene), under ultrasonic fatigue testing. Three controlled actions were implemented in order to...