Experimental measurement and model validation of COD in pipe under bending with off-centered circumferential crack
Journal Title: Frattura ed Integrità Strutturale - Year 2014, Vol 8, Issue 28
Abstract
The leak area of circumferential through-thickness crack in pipe under bending depends on the position of the crack with respect to the bending plane. In leak-before-break (LBB) analysis, the assumption that the crack is symmetrically placed with respect to the bending plane is not necessarily conservative. In this work, the crack opening of circumferential cracks, off-centered with respect to the bending plane, was investigated experimentally. Here, three pipe geometries and two crack lengths were investigated. For each crack, the centred and two off-centered configuration were examined. The crack opening displacement (COD) distribution along the crack length was measured for two selected bending load levels using digital image correlation (DIC) technique. These measurements have been used for verifying the solution provided by the hodograph cone method (HCM) as proposed by Bonora [1].
Authors and Affiliations
Domenico Gentile, G. Iannitti, Nicola Bonora
A finite-element approach for the analysis of pin-bearing failure ofcomposite laminates
In this paper, a numerical home-made finite element model for the failure analysis of bolted jointsbetween fiber-reinforced composite laminates is presented. The model is based on an incremental displacementbasedap...
Influence of temperature and exploitation period on fatigue crack growth parameters in different regions of welded joints
The influence of exploitation period and temperature on the fatigue crack growth parameters in different regions of a welded joint is analysed for new and exploited low-alloyed Cr-Mo steel A-387 Gr. B. The pa...
Plastic zone evolution near a crack tip and its role in environmentally assisted cracking
This paper analyzes the effects of crack tip plastic strains and compressive residual stresses, created by fatigue pre-cracking, on environmentally assisted cracking of pearlitic steel subjected to localized anodic...
The interface between metallurgy and mechanics in material performance
[u][/u]This paper considers an important topic, and one that is often poorly understood or misinterpreted, but which is a determining factor in many aspects of the service performance of metals (and other materials). En...
L’importanza del “parametro energetico” temperatura per la caratterizzazione dinamica dei materiali
Le esperienze maturate nel campo dell’analisi termica di materiali utilizzati nelle costruzioni meccaniche [1,2,3] hanno permesso di evidenziare come il rilievo della temperatura (terzo parametro) in prove statiche e din...