Fatigue crack propagation in turbine disks of EI698 superalloy
Journal Title: Frattura ed Integrità Strutturale - Year 2013, Vol 7, Issue 24
Abstract
In-service fatigue cracking of turbine disks of EI698 superalloy is discussed based on crack growth analyses. In the bolt joint for disks to shaft connecting there is high level of stress-state, which directed to earlier in-disks fatigue crack origination in low-cycle-fatigue regime. Fracture surface pattern such as fatigue striations were used for their spacing measurement and crack growth duration estimating. Developed disk tests on a special bench by the equivalent program to in-service cyclic loads have allowed discovering one-to-one correlation between fatigue striation spacing and crack increment in one flight. Number of fatigue striations and beach-marks calculations permitted to estimate crack growth period for the different stages of in-service disks cracking. Equivalent stress level for in-service cracked disks was calculated and compared with stress-level in-tested disks under stress equivalent program to in-service operated cyclic loads. Based on this result non-destructive inspection intervals were discussed and recommended for in-service disks in dependence on number of their flights at the moment of developed inspection to exclude in-flight disks fast fracture.
Authors and Affiliations
A. A. Shanyavskiy
Keywords
Related Articles
- EP ID EP93176
- DOI 10.3221/IGF-ESIS.24.03
- Views 69
- Downloads 0
A simple beam model to analyse the durability of adhesively bondedtile floorings in presence of shrinkage
A simple beam model for the evaluation of tile debonding due to substrate shrinkage is presented.The tile-adhesive-substrate package is modeled as an Euler-Bernoulli beam laying on a two-layer elasticfoundation. An...
Field Load Acquisition and variable amplitude fatigue testing on maxi-scooter motorcycles
Aim of the present work was the instrumentation of a maxi scooter for the field collection of service loads acting on the scooter main components such as frame, fork, handlebar, rear frame and suspension. Service...
Understanding the edge crack phenomenon in ceramic laminates
Layered ceramic materials (also referred to as “ceramic laminates”) are becoming one of the most promising areas of materials technology aiming to improve the brittle behavior of bulk ceramics. The utilization&nbs...
Experimental estimation of the heat energy dissipated in a volume surrounding the tip of a fatigue crack
Fatigue crack initiation and propagation involve plastic strains that require some work to be done on the material. Most of this irreversible energy is dissipated as heat and consequently the material temperature&...
A brittle fracture criterion for PMMA V-notches tensile specimens based on a length-enriched eXtended Finite Element approach
A criterion for the prediction of the static failure loads in tensile PMMA specimens with sharp notches is presented. The proposed criterion is based on a regularized version of the eXtended Finite Element Method (XFEM),...