Fatigue cracking of aluminium alloy AlZn6Mg0.8Zr subjected to thermomechanical treatment
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 35
Abstract
The paper presents the results of experimental test of the fatigue of aluminium alloy type AlZn6Mg0,8Zr exposed to various low temperature thermomechanical treatment. Basquin’s characteristics of fatigue have been determined in mechanical test on smooth specimens at a simple state of loading in conditions of alternating bending. The tests were carried out on a fatigue test stand constructed by the authors – MZGS 100. The development of fatigue cracking has been described based on metallographic and fractographic investigations of the fractured samples making use of a scanning electron microscope (SEM). The results of qualitative microfractography of the tested samples in the low-cycle temporal range of fatigue strength revealed fractures of the transcrystalline quasi-cleavage type. It has also been found that local effects of intercrystalline brittle cracking of this type do occur.
Authors and Affiliations
A. Kowalski, W. Ozgowicz, M. Kurek, T. Łagoda
Keywords
Related Articles
- EP ID EP148953
- DOI 10.3221/IGF-ESIS.35.51
- Views 60
- Downloads 0
Fracture morphology and its evolution A review on crack path stability and brittle fracture along butt-weld
Considerations are made for the fracture morphology and its evolution in relation to the brittle fracture along butt-weld, where crack path stability may play important roles in various aspects. Analyses of a ...
A study of white etching crack formation by compression-torsion experiments
In this study, an attempt was made to recreate the bearing damage phenomenon “White Etching Cracks” with a simplified testing setup. Rolling contact fatigue conditions were simulated with in-phase and out-ofphase...
High magnification crack-tip field characterisation under biaxial conditions
This work presents a novel methodology for characterising fatigue cracks under biaxial conditions. The methodology uses high magnification Digital Image Correlation (DIC) technique for measuring displacement and s...
A non-linear procedure for the numerical analysis of crack development in beams failing in shear
In this work, a consistent formulation for the representation of concrete behavior before and after cracking has been implemented into a non-linear model for the analysis of reinforced concrete structures, nam...
High temperature fatigue tests and crack growth in 40CrMoV13.9 notched components
The present paper addresses experimentally the high temperature fatigue of 40CrMoV13.9 steel and the effect of surface roughness on fatigue strength and crack initiation. The 40CrMoV13.9 steel is widely used in d...