Fatigue of weld ends under combined in- and out-of-phase multiaxial loading
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 38
Abstract
Weld start and end points are fatigue failure sensitive locations. Their fatigue behaviour especially in thin sheet structures under multiaxial load conditions is not sufficiently explored so far. Therefore, a research project was initiated to increase the knowledge concerning this topic, which is of special interest in the automotive industry. In the present study, fatigue tests on welded joints were conducted. In the numerical part of the study, notch stresses were calculated with an idealised weld end model. A numerical method which combines the geometrical and statistical size effect to an integrated approach was used, in order to consider the size effects
Authors and Affiliations
E. Shams , M. Vormwald
Keywords
Related Articles
- EP ID EP90975
- DOI 10.3221/IGF-ESIS.38.15
- Views 100
- Downloads 0
Photoelastic stress analysis assisted evaluation of fracture toughness in hydrothermally aged epoxies
The present work has investigated the fracture toughness of a model DGEBA epoxy system subject to Hidro-Thermal aging. A Photoelastic Stress Analysis technique has been implemented, showing the evolution of stres...
Wedge splitting test method: quantification of influence of glued marble plates by two-parameter fracture mechanics
In the present paper, the well-known wedge splitting test (WST) is applied on specimens with different geometries (S= 150, 200, 300 mm) and variants of the specimens’ configurations. K-calibration (B1) and T-stre...
Crack path in liquid metal embrittlement:experiments with steels and modeling
We review the recent experimental clarification of the fracture path in Liquid Metal Embrittlement with austenitic and martensitic steels. Using state of the art characterization tools (Focused Ion Beam and T...
Fatigue crack initiation and propagation in lotus-type porous material
The investigation of fatigue strength of lotus-type structure with nodular cast iron as a base material using computational model is analysed in present study. The irregular pores distribution in transversal and&n...
Can Keff be assumed as the driving force for fatigue crack growth?
This work raises some new questions about the validity of blindly assuming that Elber’s effective stress intensity factor is the actual fatigue crack driving force, and that as so it can be used to explain all loa...