Photoelastic stress analysis assisted evaluation of fracture toughness in hydrothermally aged epoxies
Journal Title: Frattura ed Integrità Strutturale - Year 2014, Vol 8, Issue 30
Abstract
The present work has investigated the fracture toughness of a model DGEBA epoxy system subject to Hidro-Thermal aging. A Photoelastic Stress Analysis technique has been implemented, showing the evolution of stresses arising throughout the water uptake process due to the non-uniform swelling of the material. Gravimetric and Dynamic Mechanical Thermal Analyses have further complemented the characterization, showing the onset of plasticization effects with aging. The correlation of all previous characterizations has allowed to conclude that an increase of KIC fracture toughness is obtained at the fully saturated condition. In particular Photoelasticity has also revealed the onset of relevant swelling induced stresses during the first stages of water absorption, leading to an increase of fracture toughness due to compressive stresses settling near the crack tip. A stress free condition is instead reestablished at the later stages of absorption, suggesting that the increased toughness of the saturated material is an effect of the modifications induced by aging on the polymer structure.
Authors and Affiliations
G. Pitarresi, A. Toscano, M. Scafidi, S. Alessi
Keywords
Related Articles
- EP ID EP99994
- DOI -
- Views 43
- Downloads 0
Integrity and life estimation of turbine runner cover in a hydro power plant
This paper presents integrity and life estimation of turbine runner cover in a vertical pipe turbines, Kaplan 200 MW nominal output power, produced in Russia, and built in six hydro-generation units of hydroelect...
Transverse strength of railway tracks: part 2. Test system for ballast resistance in line measurement
In the present paper, testing methods currently adopted to measure the in service ballast resistance are synthetically reviewed to identify the main sources of uncertainty influencing the test loads and to define...
A probabilistic interpretation of the Miner number for fatigue life prediction
The Miner number M, used as a tool for lifetime prediction of mechanical and structural components in most of the standards related to fatigue design, is generally accepted as representing a damage stage resultin...
Models of initiation fatigue crack paths proposed by Macha
Professor E. Macha devoted his academic life to solving the problems connected with random multiaxial fatigue in components of machines and structures. In his studies he formulated stress, strain and energy crite...
Damage tolerance analysis of aircraft reinforced panels
This work is aimed at reproducing numerically a campaign of experimental tests performed for the development of reinforced panels, typically found in aircraft fuselage. The bonded reinforcements can significantly reduce...