Multiaxial fatigue of in-service aluminium longerons for helicopter rotor-blades
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 37
Abstract
Fatigue cracking of longerons manufactured from Al-alloy AVT-1 for helicopter in-service rotorblades was considered and crack growth period and equivalent of tensile stress for different blade sections were estimated. Complicated case of in-service blades multiaxial cyclically bending-rotating and tension can be considered based on introduced earlier master curve constructed for aluminum alloys in the simple case of uniaxial tension with stress R-ratio near to zero. Calculated equivalent tensile stress was compared for different blade sections and it was shown that in-service blades experienced not principle difference in this value in the crack growth direction by the investigated sections. It is not above the designed equivalent stress level. Crack growth period estimation in longerons based on fatigue striation spacing or meso-beach-marks measurements has shown that monitoring system introduced designer in longerons can be effectively used for in-time crack detecting independently on the failed section when can appeared because of various type of material faults or in-service damages.
Authors and Affiliations
A. Shanyavskiy
Keywords
Related Articles
- EP ID EP159462
- DOI 10.3221/IGF-ESIS.37.04
- Views 65
- Downloads 0
A link between the peak stresses and the averaged strain energy density for cracks under mixed-mode (I+II) loading
In this work, a link between the averaged strain energy density (SED) approach and the peak stress method in the case of cracks subjected to mixed mode (I+II) loading has been investigated. Some closed-form e...
EBSD-assisted fractographic analysis of crack paths in magnesium alloy
Magnesium (Mg) alloys are attractive as structural materials due to their light weight and high specific strength. It is well known that Mg alloy has hexagonal close-packed (HCP) structure and only basal slip ...
Design and experimental characterization of a 350 W High Temperature PEM fuel cell stack
High Temperature Proton Exchange Membrane (HT PEM) fuel cell based on polybenzimidazole (PBI) polymer and phosphoric acid, can be operated at temperature between 120 °C and 180 °C. Reactants humidification is not require...
High-cycle fatigue strength of a pultruded composite material
Dealing with composites in polymeric matrix, the pultruded ones are among the more suitable for large production rates and volumes. For this reason, their use is increasing also in structural applications in civil and...
Near tip strain evolution of a growing fatigue crack
Near tip full-field strains in a growing fatigue crack have been studied in situ using the Digital Image Correlation (DIC) technique in a compact tension specimen of stainless steel 316L under tension-tension cycl...