New Golden Red Sodium Calcium Silicate Glasses
Journal Title: International Journal of Structural Glass and Advanced Materials Research - Year 2017, Vol 1, Issue 1
Abstract
Traditional golden red glasses were based on K2O-PbO-SiO2 composition system. In this paper, we reported new golden red glasses based on Na2O-CaO-SiO2 system without SnO2 and PbO in them. By using a spectrophotometer and chromamter color difference meter, it was found that the new glasses had similar optical properties to the traditional ones. The diameter of the gold particles in new glasses is around 40 nm determined by scanning electron microscope. The surface plasmon resonance created by the absorption of visible light emits golden red color. The benefits of using new golden red sodium calcium silicate glasses are the reductions of gold amount, cost and lead pollution to the environment.
Authors and Affiliations
Wang Cheng-Yu, Wun Nuan-Xin, Ge Yi, Tang Hua-Juan and Wang Paul W
Effect of Novel Thermo-Chemical Treatment on Bending Strength of Laminated Glass
The science of thermal and chemical treatment of glass is well documented. The Laminated Glass (LG) is usually not treated as either treated glass is used during production or lower melting temperature of interlayer does...
Influence of Acid Frosting on the Microstructure Characteristics and Mechanical Strength of Eroded Soda-Lime-Silica Glasses by Sandstorm
Most glass products such as cars windshields, solar panels protecting glass and windowpanes are exposed to unavoidable sandblasting effects especially in areas prone to sandstorms. This sand impingement results into micr...
Nonlinear Analysis of RC Box Culverts Resting on a Linear Elastic Soil
In the analyses presented, the soil-structure interaction is accounted for by means of a FE-BIE approach, in which the structure is modelled with displacement-based beam finite elements, whereas the boundary between stru...
Transformable Curved Thin Glass Greenhouse
The use of new generation thin, lightweight and damage-resistant glass, originally conceived for electronic displays, is being very recently proposed for structural applications, in particular for adaptive and movable sk...
Preparation of Porous Silicon P-Type and Thermal Diffusivity Measurement Using Photoacoustic Technique
Porous silicon (PSi) layers were formed on a p-type Si wafer. Electrochemical method was used to prepare 36 samples with three values of current density (10, 20 and 30) mA/cm2, each involved ( 20, 40, 60 and 80) min etch...