PITTING CORROSION OF STAINLESS STEEL AT THE VARIOUS SURFACE TREATMENT
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2011, Vol 18, Issue 4
Abstract
The stainless steel surface treatment is very important with regard to its pitting corrosion susceptibility. An effect of various types surfacing on pitting corrosion resistance of AISI 304stainless steel is investigated in this work. The samples of the tested material are turned, blasted, peened, grinded and a half of them are pickled to achieve higher purity of surfaces and better quality of passive film. Eight types of different finished surfaces are tested by electrochemical and immersion tests to determine corrosion behaviour in conditions where pitting is evoked by controlled potential and second by solution with high redox potential. By this way the effect of mechanical and chemical surface treatment on the resistance to pitting corrosion, character, size and shape of pits are compared in the conditions of different mechanisms of corrosion process.
Authors and Affiliations
Viera Zatkalíková, Tatiana Liptáková
Keywords
Related Articles
- EP ID EP102956
- DOI -
- Views 107
- Downloads 0
Cyclic plastic behavior and fatigue life of AZ91 alloy in as-cast and ultrafine-grained state
Fatigue properties of magnesium alloy AZ91 in as-cast and in ultrafine-grained state prepared by equal channel angular pressing were investigated. The fatigue strength in the low-cycle fatigue region was found to be subs...
EXPERIMENTAL INVESTIGATION OF EROSIVE WEAR ON THE HIGH CHROME CAST IRON IMPELLER OF SLURRY DISPOSAL PUMP USING RESPONSE SURFACE METHODOLOGY
Erosive wear occurs on the impeller and volute casing of the slurry disposal pump due to the impact of the ash particles on the impeller with a high velocity. Due to erosive wear, pump life become very short. The service...
THE EFFECT OF REFLOW ON WETTABILITY OF Sn 96.5 Ag 3 Cu 0.5 SOLDER
Surface conditions on Printed Circuit Board (PCB) final finishes have an important impact on the wetting behavior with lead-free solder. The improvement of the wettability in liquid Sn 96.5 Ag 3 Cu 0.5 Solder alloy on PC...
MEASUREMENT OF QUENCHING INTENSITY, CALCULATION OF HEAT TRANSFER COEFFICIENT AND GLOBAL DATABASE OF LIQUID QUENCHANTS
This paper explains the need for a database of cooling intensities for liquid quenchants, in order to predict the quench hardness, microstructure, stresses and distortion, when real engineering components of complex geom...
INTERNAL FRICTION USE IN MONITORING THE DEGRADATION PROCESSES IN A MATERIAL
During the measurement of the fatigue life of material, the specimen undergoes large number of stress cycles. While the observed number of cycles before failure is considered to be the most important result (often the on...