Plastic properties of cold-deformed ironbased sintered materials
Journal Title: Archiwum Odlewnictwa - Year 2010, Vol 10, Issue 3
Abstract
Cold plastic forming of sintered metal powders has limited practical application because of, among others, the deformation degree and initial porosity of preforms. Cold forming is combined with a very drastic drop of plastic properties observed in final products. One of the methods that enable regaining the lost plasticity is annealing of sinters after deformation at temperatures above the recrystallisation point. The results of the investigations were presented which aimed at the determination of an effect that the annealing conditions of colddeformed sintered metal powder can have on its structure and mechanical properties. Special attention was drawn to a combined effect of the deformation degree and heat treatment temperature on final plastic properties of the sinters and on their ultimate tensile strength.
Authors and Affiliations
K. Zarębski, S. Okoński, P. Putyra, A. Tabor
Keywords
Related Articles
- EP ID EP72126
- DOI -
- Views 112
- Downloads 0
Influence analysis foamed polystyrene model on casting defects as well as microstructure ductile cast iron from Lost Foam process with Inmold method
In this work was shown a influence analysis foamed polystyrene model on casting defects as well as microstructure ductile cast iron from Lost Foam process with Inmold method.
Heat transfer analysis during cooling of die with use of water mist
The paper presents the results of the heat transfer area during the cooling process of steel test die with water mist which consist the flow of air in the range 150÷350 l/min and 0.050.24 l/min of water. Temperature cha...
Usage of Connor Inlets to Eliminate Shrinkage
The demand for castings of high quality and sound work is nowadays very high. The production of sound castings without foundry errors is the big issue in modern foundries. Foundry simulation software can do a lot to help...
Fatigue damage cumulation in brass under variable loading
In the paper there was presented the course of fatigue damage cumulation in specimens made of CuZn37 brass. During the analysis the course of damage cumulation there were used parameters of hysteresis loop and microstruc...
Influence of vibrations during crystallization of EN AC-ALSi13Cu2 alloy on mechanical and porosity properties
Today’s industry aims at such situation, where number of defective products, so called defects shall approach to zero. Therefore, one introduces a various changes in technology of production, introduces improvements whic...