RESIDUAL LIFE OF REPAIR WELDED JOINTS IN PIPELINES MADE OF 13HMF AFTER USE FOR THE DESIGN OPERATING TIME
Journal Title: Prace Instytutu Metalurgii Żelaza - Year 2018, Vol 70, Issue 3
Abstract
This paper presents the results of material tests of repair welded joints carried out for samples of materials taken from high pressure steam pipelines after over 200,000 operating hours in creep conditions, made of the 13HMF steel (14MoV6-3). The aim of the study was to assess the mechanical properties and changes in the structure of repair welded joints (new material + material after use), including the original material, heat affected zone and the weld, occurring as a result of the welding process and heat treatment after welding.
Authors and Affiliations
Artur Jasiński, Adam Zieliński, Hanna PURZYŃSKA
Keywords
Related Articles
- EP ID EP432148
- DOI 10.32730/imz.0137-9941.18.3.01
- Views 78
- Downloads 0
MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A SIMILAR T24 STEEL WELDED JOINT AFTER SERVICE
The material under investigation was a welded joint made of 7CrMoVTiB10-10 (T24) steel after 36,000 hours of use at the temperature of 540°C and pressure of 27 MPa. The test samples for the study were taken from a membra...
WYBRANE WŁAŚCIWOŚCI MECHANICZNE I TECHNOLOGICZNE WYSOKOWYTRZYMAŁYCH NANOSTRUKTURALNYCH STALI BAINITYCZNYCH
W artykule omówiono zagadnienie optymalizacji parametrów technologicznych wytwarzania stali nanostrukturalnej umożliwiających skrócenie czasu wygrzewania izotermicznego oraz uzyskanie wysokiej wytrzymałości i plastycznoś...
APPROACH TO FERROMAGNETIC SATURATION FOR AMORPHOUS FE-BASED ALLOY
The paper presents the results of research on the structure and selected properties of magnetic alloys based on Fe. The alloy with the chemical composition Fe36Co36Y8B20 was produced using two methods: forcing and suckin...
RESIDUAL LIFE OF REPAIR WELDED JOINTS IN PIPELINES MADE OF 13HMF AFTER USE FOR THE DESIGN OPERATING TIME
This paper presents the results of material tests of repair welded joints carried out for samples of materials taken from high pressure steam pipelines after over 200,000 operating hours in creep conditions, made of the...
OPRACOWANIE MODELI KRAJOWEGO ZUŻYCIA PRĘTÓW ŻEBROWANYCH W LATACH 2004–2017 Z UWZGLĘDNIENIEM RYNKU CEMENTU I KATEGORII OBIEKTÓW BUDOWLANYCH
Celem niniejszej publikacji jest opracowanie modeli ekonometrycznych określających zależności między zużyciem prętów żebrowanych (zmienna objaśniana) w krajowym budownictwie w latach 2004–2017 i materiałami substytucyjny...