Study of Formation of Oxide Nanostructures on the Surface of Radiation-oxidated Aluminum
Journal Title: Materials Science: Materials Review - Year 2018, Vol 2, Issue 1
Abstract
Reflection IR spectroscopy, atomic force microscopy (AGM), and electrophysical measurements were used to investigate the formation of surface oxide nanostructures during the radiation oxidation of metallic aluminum in contact with water. It is revealed that the radiation modification of the surface relief is accompanied by the formation of oxide nanolayers, the defectiveness of which is determined by the irradiation time. It is shown that the formation of oxide nanolayers in the region of absorbed dose (0.5-120 kGy) occurs in three stages, which is accompanied by a decrease in electrical conductivity by 5 orders and an increase in the thickness of the oxide layer by an order of magnitude. The role of surface intermediate-active particles in the formation of oxide nanostructures is considered.
Authors and Affiliations
Gadzhieva N. N
Keywords
Related Articles
- EP ID EP679042
- DOI -
- Views 165
- Downloads 0
Polyethylene plastic production process
Polyethylene has become the most important polyolefin plastic with excellent mechanical properties, processing properties and chemical resistance. It is used in the production of film, packaging and pipe. However, the no...
Behavior of Cast {TI or Ta}-Containing Alloys Based on Nickel and/or Cobalt in High Temperature Oxidation: Effect of the Ni/Co Ratio
Many of the cast superalloys chosen for specific applications at high temperatures, such as tools devoted for shaping molten glass, are based on nickel or cobalt. They contain chromium and carbon to achieve good resistan...
The development of polyurethane
Polyurethane is one of the six promising synthetic materials in the world. Due to its excellent product performance and wide application field, it is a crucial industry of development in the world. This paper introduces...
Preparation and Study of Waterborne Asphalt Pavement Maintenance Agent
The precursor Ni0.76Co0.1Mn0.1 (OH) 2 was prepared by coprecipitation method. The precursor was mixed with Mg (OH) 2 / Zn (NO3) 2 / TiO2 and LiOH.H2O, Li2CO3 to synthesize doped lithium Ion layer positive electrode mater...
Cooling Rate, Hardness and Microstructure of Aluminum Cast Alloys
This experiment investigated the cooling curve behavior, hardness and microstructure of two aluminum alloys produced by casting process. There are Al-1.37Zn-1.19Si and Al-1.66Si-1.35Zn derived from melting and alloying a...