STUDY OF SELECTED USABLE PROPERTIES OF THE TOP LAYERS OF WELD OVERLAYS PRODUCED BY LASER TECHNOLOGY FOR APPLICATIONS IN THE POWER INDUSTRY
Journal Title: Tribologia - Year 2018, Vol 277, Issue 1
Abstract
The paper presents the results of laboratory tests of test specimens produced by multi-layer laser padding alloy Stellit Co-6 powder on a substrate with heat-treated X22CrMoV12-1 alloy steel. Multilayer laser padding was performed on a TRUMPF TruLaser Cell 3008. The formed weld overlays surface was studied using an optical microscope. Selected usable properties, such as surface topography, microstructure, hardness and erosion resistance were studied. During the analysis, areas of cross-sections test specimens after multilayer laser padded, in the connection zone of the substrate material with weld overlay, no cracks and no discontinuities in weld overlay were found in the substrate. As a result of conducted experiments, regular, repetitive weld overlays with characteristic directional crystallization were obtained. A microstructure with different growth directions with respect to the surface of the substrate shaped coniferous dendrites was obtained. The hardness of the weld overlays was in the range from 420 to 620 HV0.1, and in the heat affected zone, in the range of 320 to 420 HV0.1. Significant increases in erosion resistance of the surface layer of Stellite type Co-6 weld overlay produced by laser in comparison with the parent material after hardening were found.<br/><br/>
Authors and Affiliations
Wojciech NAPADŁEK, Adam WOŹNIAK
Keywords
Related Articles
- EP ID EP346182
- DOI 10.5604/01.3001.0011.9932
- Views 53
- Downloads 0
ANALIZA WPŁYWU PARAMETRÓW DRGAŃ STYCZNYCH I PRĘDKOŚCI POŚLIZGU NA SIŁĘ TARCIA W RUCHU ŚLIZGOWYM
W pracy przedstawiono wyniki analiz symulacyjnych i badań doświadczalnych wpływu kierunku i parametrów drgań stycznych oraz prędkości poślizgu na siłę tarcia i siłę napędu w ruchu ślizgowym. Omówiono wykorzystane w anali...
Właściwości tribologiczne anodowych warstw tlenkowych modyfikowanych cząstkami węgla i nanorurkami
DETERMINATION OF LUBRICITY PROPERTIES OF HYDROCRACKED DIESEL BASE FUEL AS THE FUNCTION OF THE CONCENTRATION OF CHO ADDITIVES PART IV
Part 1 of the investigated subject field contains the initial methodical results. Part 2 generally describes basis of the thematic area: findings of the tribological proprieties of ester additives CHO (carbon, hydrogen,...
Kompleksowe porównanie modelowych kompozycji olejowych na bazie oleju mineralnego, syntetycznego, białego i naturalnego
Celem prac było sprawdzenie możliwości zastosowania oleju naturalnego i białego jako bazy olejów przekładniowych. Testom poddano cztery modelowe oleje przekładniowe – z bazą mineralną, syntetyczną węglowodorową (PAO), bi...
WYZWANIA I METODY W ANALIZACH PRZEPŁYWU CIEPŁA W BEZSMAROWYCH ŁOŻYSKACH POLIMEROWYCH
Generacja ciepła i jego rozprowadzenie stanowi ważny element przy projektowaniu i użytkowaniu suchych łożysk polimerowych, ponieważ wysoka temperatura może prowadzić do szybszego zużycia materiału i uszkodzenia łożyska....