Synthesis of Carbon-Silica Nanomaterials by Carbonization of Cellulose Acetate and Polyisocyanate Copolymer
Journal Title: Фізика і хімія твердого тіла - Year 2016, Vol 17, Issue 2
Abstract
Cellulose acetate and polyisocyanate copolymer synthesized by mechanical mixing of cellulose acetate, polyisocyanate and fumed silicon dioxide in the presence of nickel chloride was carbonized in silicon dioxide template. Copolymer and silicon dioxide template were formed simultaneously. Composite structure and composition was studied with SEM and EDS. SEM showed that porous carbonaceous nanomaterial was synthesized. Formed carbon is represented by coating on silicon dioxide, layered ribbon-like and fibrous structures in template pores with size from several nm (thickness) to several microns (length). Metallic nickel crystals up to 200 nm in size were fabricated in composite pores from Nickel chloride by reduction of Ni2 with products of pyrolysis of organic compounds.
Authors and Affiliations
V. V. Goncharuk, V. M. Ogenko, L. V. Dubrovina, D. D. Kucheruk, O. V. Naboka, I. V. Dubrovin
Keywords
Related Articles
- EP ID EP255189
- DOI 10.15330/pcss.17.2.241-246
- Views 51
- Downloads 0
Electrophysical Properties of Indium Doped As2(S, Se)3 thin Films
The electrical studies of In-doped thin films based glassy As2S3 and As2Se3, determined the energy of activation, the analysis of photovoltaic memory samples.
Synthesis of Carbon-Silica Nanomaterials by Carbonization of Cellulose Acetate and Polyisocyanate Copolymer
Cellulose acetate and polyisocyanate copolymer synthesized by mechanical mixing of cellulose acetate, polyisocyanate and fumed silicon dioxide in the presence of nickel chloride was carbonized in silicon dioxide template...
Electrical Conductivity and Magnetoresistance of Silicon Microstructures in The Vicinity to Metal-Insulator Transition
Complex research of silicon microcrystals with specific resistance from ρ<sub>300K</sub> = 0.025 Ohm × cm to ρ<sub>300K</sub> =0.007 Ohm × cm doped with boron transport impurity to concentrations corresponding to the tr...
Synthesis of CdS Nanocrystalsin the Gelatin Matrix with Different рН Values and their Optical Properties
We have investigated the influence of solution pH on the formation of nanocrystals and their size in the process of synthesis. We have analyzed the optical absorption spectra and luminescence of colloidal solutions of NC...
Crystalchemistry Models of Defect Subsystem in Nonstoichiometric Cadmium Telluride Crystals
Analysis of the defective subsystems in clean cadmium telluride was performed using methods of crystal chemistry. There were developed crystalquasichemical formulae for the non-stoichiometric n-CdTe, p-CdTe crystals, det...