Synthesis of Cox Ni1-XFe2 o4 (X = 0.0, 0.5, 1.0) Nanoparticles by Chemical Co-Precipitation Route
Journal Title: International Journal of Nano Studies & Technology (IJNST) - Year 2014, Vol 3, Issue 5
Abstract
Magnetic nanoparticles (NPs) of nickel-cobalt ferrite (Cox Ni1-xFe2 O4 ; x = 0.0, 0.5, 1.0) were synthesized by co-precipitation route. The chemicals used were nickel chloride, cobalt chloride, ferric chloride, sodium hydroxide, and oleic acid. Sodium hydroxide was used as the precipitating agent and oleic acid was used as the surfactant. X-ray diffraction (XRD) analysis confirmed the formation of single phase nickel-cobalt ferrite nanoparticles in the size range 12-20 nm. The obtained size of the nanoparticles is depending on the variation of different reaction parameters during the reaction and annealing time and temperature after the reaction. Hysteresis loops of the samples confirmed the magnetic characteristics of the prepared (Cox Ni1-xFe2 O4 ; x = 0.0, 0.5, 1.0) nanoparticles.
Authors and Affiliations
K. Maaz
Keywords
Related Articles
- EP ID EP201482
- DOI 10.19070/2167-8685-1400011
- Views 66
- Downloads 0
Self-Assembled Microwires of Aromatic Acids and Melamine
Self-assembled micro/nanowires of melamine and seveal aromatic acids, including thiocyanuric acid, trimesic acid, terephthalic acid, and 5-sulfoisophthalic acid, are formed through evaporation of water in a solution mixt...
Synthesis and Characterization of Ultrafine and Porous Structure of Magnesium Ferrite Nanospheres
Porous sphere-shaped magnesium (MgFe2 O4 ) spinel ferrite particles were synthesized with high yields, crystallinity and purity through an easy, quick, reproducible and low-temperature hydrothermal synthesis route starti...
Brief Review on Some Major Factors Affecting Visible Light Activity of Titania Photocatalyst
As sunlight is an excellent source of clean energy, research for harnessing the energy via an efficient photocatalyst that is active under visible light is actively underway. Titania is well accepted as a photosemiconduc...
3D Simulation of Fin Geometry Influence on Corner Effect in Multifin Dual and Tri-Gate SOI-Finfets.
In this work the corner effect sensitivity to fin geometry variation in multifin dual and tri-gate SOI-FinFETs is studied through a commercial, three-dimensional numerical simulator ATLAS from Silvaco International [1]....
Fabrication and Magnetoresistance of Single Au-Ni-AuNanowire
Magnetoresistance of Au-Ni-Aunanowire with 300 nm long nickel segment sandwiched between the gold segmentsis studied. Structural analysis of the sample is performed by X-ray diffraction and transmission electron microsco...