Synthesis of high molecular weight polyethylene using FI catalyst

Journal Title: Polyolefins Journal - Year 2014, Vol 1, Issue 1

Abstract

A FI Zr-based catalyst of bis[N-(3,5-dicumylsalicylidene)-2′,6′­diisopropylanilinato]zirconium(IV) dichloride was prepared and used for polymerization of ethylene. The effects of reaction conditions on the polymerization were examined in detail. The increase in ethylene pressure and rise in polymerization temperature up to 35 oC were favorable for catalyst/MAO to raise the catalytic activity as well as the viscosity-average molecular weight (Mv) of polyethylene. The activity of the catalyst was linearly increased with increasing MAO concentration and no optimum activity was observed in the range studied. Although introduction of the bulky cumyl and 2′,6′-diisopropyl alkyl substitution groups on ortho positions to the phenoxy-oxygen and on phenyl ring on the N, respectively enhanced the viscosity average molecular weight (Mv) of the obtained polymer strongly, diminished the activity of the catalyst. Neither the activity of the catalyst nor the (Mv) of the obtained polymer were sensitive to hydrogen concentration. However, higher amount of hydrogen could slightly increase the activity of the catalyst. The (Mv) of polyethylene ranged from 2.14×106 to 2.77×106 at the monomer pressure of 3 and 5 bar respectively which are much higher than that of the reported FI Zr-based catalysts.

Authors and Affiliations

G. Hossein Zohuri, Saman Damavandi, Saeid Ahmadjo, Reza Sandaroos, Mohammad A. Shamekhi

Keywords

Related Articles

How can pH value during catalyst preparation affect the performance of vanadium-modified (SiO2/MgO/ MgCl2)•TiClx Ziegler-Natta polyethylene catalysts

Vanadium-modified (SiO2/MgO/MgCl2)•TiClx Ziegler-Natta catalysts were prepared through co-impregnation of water-soluble magnesium and vanadium salts under different pH values. Several key factors such as pH value of co-i...

The relationship among changes in microstructure, active sites behavior and properties in the propylene polymerization with a 4th generation Ziegler-Natta catalyst

Three polypropylene samples (1-3) were synthesized with a 4th generation Ziegler-Natta catalyst in the presence of cyclohexyldimethoxymethylsilane (donor c), dicyclopenthyldimethoxysilane (donor d) and diisopropyldimetho...

Kinetics of ethylene polymerization over titanium-magnesium catalysts: The reasons for the observed second order of polymerization rate with respect to ethylene

The data on the effect of ethylene concentration on polymerization rate for several modifications of modern highly active titanium–magnesium catalysts TiCl4/MgCl2 are presented. These catalysts differ in titanium content...

Production of titanium tetrachloride (TiCl4) from titanium ores: A review

Titanium (Ti) is the ninth most abundant element on earth. The titanium mineral ores are widely distributed in different parts of the world. The two main ores of titanium include rutile (TiO2) and ilmenite (FeO.TiO2). It...

Propene-cycloolefin polymerization

Highly active metallocenes and other single site catalysts have opened up the possibility of polymerizing cycloolefins such as norbornene (N) or of copolymerizing them with ethene (E) or propene (P). The polymers obtaine...

Download PDF file
  • EP ID EP283045
  • DOI 10.22063/POJ.2014.925
  • Views 143
  • Downloads 0

How To Cite

G. Hossein Zohuri, Saman Damavandi, Saeid Ahmadjo, Reza Sandaroos, Mohammad A. Shamekhi (2014). Synthesis of high molecular weight polyethylene using FI catalyst. Polyolefins Journal, 1(1), 25-32. https://europub.co.uk/articles/-A-283045