Temperature Dependence of Initial Permeability of NixCo1-xFe2O4 Ferrite System
Journal Title: Фізика і хімія твердого тіла - Year 2015, Vol 16, Issue 4
Abstract
The aim of this work was to create and study of ferrite nickel-cobalt powders, using sol-gel technology with participation of auto-combustion. Dependence of the initial permeability from the degree of substitution of cobalt cations on nickel cations is obtained. It is revealed that the crystallite size has a significant influence on the magnetic properties of the samples. With decreasing of crystallite size of nickel-cobalt ferrite Curie temperature decreases. It is shown that the smaller the particle size, the greater the thickness of the surface layer with significant violations of magnetic structure.
Authors and Affiliations
V. S. Bushkova, A. V. Kopayev, N. I. Bushkov, B. V. Karpyk Karpyk, O. M. Matkivsky
Keywords
Related Articles
- EP ID EP293211
- DOI 10.15330/pcss.16.4.695-699
- Views 59
- Downloads 0
Temperature Dependences Conductivity of Ceramics with Composition Li2O - Fe2O3 - Al2O3 from the Content of Aluminium
The method of impedance spectroscopy was used for research temperature dependences of electrophysical properties ceramic with composition Li2O-Al2O3-Fe2O3. It is shown that in general with increasing temperature conducti...
Thermodynamics of Point Defects and Homogeneity Zinc Telluride
Based on the model crystal defect subsystem zinc telluride crystals which considers possibility of the formation of neutral, singly and doubly ionization cationic and anionic vacancies calculated homogeneity ZnTe, and th...
Sistem Criate Hight Vojltag Frequency-Impuls Electric Fields for the Obtaining Stress-Strain Surface
In this article development and criate new model phizical-technical obtaining material technological equipment the method higth-friquency plazmy plating-flame carboids and nitralloy cohesion hight-temepature metal IV - V...
Thermodynamic Properties of Intermediate Phases of the Ag-Bi-Se System in the Temperature Range 535-578 K
In the galvanic elements C|Ag|AgI|glass Ag2GeS3|D|C (C – current electrodes, D – heterophase alloys of the Ag–Bi–Se system, AgI|glass Ag2GeS3 – two layer membrane with pure ionic (Ag+) conductivity) synthesis Ag with het...
The Influence of Technology Modes on “Hat Wall” Method on Structure and Electrical Properties of SnTe Films
The results of complex studies of the structure and electrical properties of vapor-phase condensation of SnTe, deposited in the method of "hot wall" on fresh chips of (111) single crystals of BaF2 by various technologica...