The Effect of Cutting Parameters on Tool Wear During the Milling of Carbon Fiber Reinforced Polymer (CFRP) Composites
Journal Title: Materials Science-Medžiagotyra - Year 2019, Vol 25, Issue 1
Abstract
Reduction of machining times and optimization of cutting parameters and conditions hold great importance in machining processes. Milling is among the most important machining processes used for machining of fiber-reinforced composite materials. The present research was carried out to investigate the effect of cutting parameters on tool wear during the milling of carbon fiber reinforced polymer (CFRP) materials which are widely used in aviation and aerospace industries. A multi-directional CFRP composite material with 6 mm width and 26 layers was used as the workpiece. The tests were performed under dry conditions on a CNC vertical processing center with 100, 200 and 300 m/min cutting speeds; 0.05 , 0.15 and 0.25 mm/tooth feedrates and at 1 mm constant cutting width. To understand the wear process, scanning electron microscopy (SEM) analyses of the worn surfaces were performed.
Authors and Affiliations
Dervis OZKAN, Mustafa Sabri GOK, Hasan GOKKAYA, Abdullah Cahit KARAOGLANLI
Keywords
Related Articles
- EP ID EP452518
- DOI 10.5755/j01.ms.25.1.19177
- Views 31
- Downloads 0
Data on Evaluation of the Corrosion Inhibition Effect of L-alpha-aminoisocaproate on High Carbon Steel Corrosion in Dilute Acid Media
Corrosion inhibition performance of l-alpha-aminoisocaproate on high carbon steel in 1 M HCl solution has been studied by weight loss measurement, open circuit potential measurement, optical microscopy and ATF-FTIR spect...
The Microstructure and Wear Resistance of the Ti-assisted Hot Plasma Nitrided Layer
In order to improve the wear resistance of the surface nitrided layer of 1060 aluminum matrix, the nitrogen containing thermal plasma Ti-assisted nitriding method was adopted to obtain the strengthening phases of AlN and...
Mössbauer Spectroscopy and Magnetic Properties of Bi0.8Ca0.2-xSrxFeO3 Nanoparticles by Sol-gel Method
Doping at A/B-sites can effectively improve the physical properties of perovskite ferrites. In this study, the performance of Bi0.8Ca0.2-xSrxFeO3 was investigated using the sol-gel autocombustion method. The results show...
Comparative Study on the Tribological Properties of AISI52100 Steel Surface Modified by Graphite/MoS2 Composite Coating and Manganese Phosphate Coating
Surface modification is an important method to improve the contact fatigue life of transmission parts. The preparation of high performance coating with good tribological properties on the gears and bearings has become th...
Curing Kinetics and Mechanism Research of E44/T31 Insulation Paint
Epoxy resin insulation paint was prepared with epoxy resin (E44) as binder and with proper inorganic fillers and curing agent (T31) as additives. The isothermal curing reaction process of paint was studied by the differe...