THE EFFECT OF DIFFERENT SURFACE TREATMENTS OF 316L STEEL ON ADHESIVE JOINT STRENGTH
Journal Title: Journal of Machine Construction and Maintenance - Year 2018, Vol 108, Issue 1
Abstract
The present paper examines selected strength test results of adhesive joints of 316L steel after different types of surface treatment. The analysis focuses on the effect of surface layer treatment on the value of selected 2D and 3D surface roughness parameters with regards to adhesive joint strength. In addition, the Abbott-Firestone curve (bearing area curve) is examined in order to provide information on the state of the surface in terms of its suitability for adhesive joining. Experimental data from shear strength tests of 316L steel specimens bonded with Loctite EA 9466 was subjected to comparative analysis. The final section draws conclusions from the study.
Authors and Affiliations
Mariusz KŁONICA
Keywords
Related Articles
- EP ID EP615723
- DOI -
- Views 112
- Downloads 0
PREDICTION OF HYDRODYNAMIC STABILITY LOSS IN WATER-LUBRICATED PLAIN BEARINGS BASED ON THE LYAPUNOV EXPONENT
The article proposes a new algorithm for data analysis for diagnostics and the prediction of the loss of hydrodynamic stability in plain bearings associated with the appearance of oil vortexes in the lubrica...
FATIGUE CHARACTERISTICS OF 6082-T6 ALUMINIUM ALLOY OBTAINED IN TENSION-COMPRESSION AND OSCILLATORY BENDING TESTS
The paper presents the comparison of the results of experimental fatigue tests for 6082-T6 aluminium alloy, carried out for two states of loading: strain controlled tension-compression, and strain and bending moment cont...
PROBLEMS OF THE COMPENSATION OF CENTRIFUGAL FORCE IN LATHE CHUCKS
Modern machining technology facilitates mechanical machining at high spindle speeds, which determines the use of machining lathe chucks that guarantee the correct clamping force of the workpiece. The work...
RMS PROCESS CONTROL ALGORITHM BASED ON THE VOLTAGE METHOD
For the last several years, considerable progress in the use of the plasma surface engineering for the purposes of the surface layer’s modification has been observed. The magnetron sputtering method is one of the most im...
TESTING OF THE STATE OF STRESSES AFTER FINISH BURNISHING ITEMS
The article presents the results of studies on the formation of residual stresses due to finish burnishing. Improper state of stresses may arise when, seeking higher dimension and shape accuracy, smaller roughness, or im...