THE EFFECT OF SURFACE TEXTURE OF STEEL DISC ON FRICTION AND FRETTING WEAR
Journal Title: Tribologia - Year 2018, Vol 280, Issue 4
Abstract
Fretting tests were performed using an Optimol SRV5 tribotester in a ball-on-flat scheme. Balls from 100Cr6 steel of 60 HRC hardness and diameters of 10 mm co-acted with discs from 42CrMo4 steel of 47 HRC hardness under dry gross fretting conditions. Tests were performed at 300C and 25–35% relative humidity, and the number of cycles was 18000. During each test, the normal load was kept constant. Six sets of experiments were conducted. Discs had different surface textures as the result of machining. It was found that the lowest coefficients of friction were obtained for anisotropic surfaces when ball movements were perpendicular to main disc texture directions.<br/><br/>
Authors and Affiliations
Agnieszka LENART, Paweł PAWLUS, Andrzej DZIERWA, Mirosław TUPAJ
Keywords
Related Articles
- EP ID EP414830
- DOI 10.5604/01.3001.0012.7527
- Views 63
- Downloads 0
AN ANALYSIS OF THE INFLUENCE OF THE TYPE OF CONTACT IN A SLIDING NODE RELATED TO THE ESTIMATION OF LUBRICATION EFFICIENCY
The paper presents experimental work on the influence of the type of contact in a sliding node related to the estimation of lubrication efficiency using greases working in a mixed lubrication area. Investigations were ca...
PROPERTIES OF CARBIDE LAYERS PRODUCED BY MEANS OF THE POWDER METHOD AT LOW PRESSURE
The paper presents the results of examinations of materials and tribological properties of chromized carbide layers produced on tool steel by means the powder method, modified by the use of low pressure during the proces...
BADANIA WPŁYWU WYBRANYCH CZYNNIKÓW NA PRĘDKOŚĆ KRYTYCZNĄ PRACY WZDŁUŻNEGO ŁOŻYSKA ŚLIZGOWEGO Z CIECZĄ MAGNETOREOLOGICZNĄ
Ciecze magnetyczne są to substancje o złożonym składzie fizykochemicznym. Unikatowe właściwości cieczy magnetycznych polegają na możliwości odwracalnej, niemal natychmiastowej zmiany ich parametrów reologicznych, jak rów...
PROPERTIES OF DUPLEX LAYERS PRODUCED IN A VACUUM CHROMIZING PROCESS ON STEEL COVERED WITH COBALT ALLOY
The paper presents the results of examinations of the structure and properties of duplex layers of the CrC+(Co-W) type, produced in a vacuum chromizing process on a tool steel surface covered with Co-W electrolytic alloy...
THE EFFECT OF AN ADDITIVE ON THE WEAR OF THE NODES WORKING IN A MIXED LUBRICATION AREA
This paper presents the results of the experimental work on the modification of the operating conditions of working nodes using three preparations: two that create ceramic layers on the surfaces of elements and one modif...