The influence of amperage of electric arc on microhardness in the area single and overlapping remeltings of HS 6-5-2 steel
Journal Title: Archiwum Odlewnictwa - Year 2011, Vol 11, Issue 3
Abstract
The present thesis depicts the microhardness of HV0,065 surface layer of high speed steel HS6-5-2 remelted with the electric arc. There were different surface layer variants of remelting used – the amperage was changed from 50 to 120A with the stable scanning speed of 300mm/min. There was also the influence of overlapping of the remeltings on the microhardness result. The highest average microhardness of the surface layer of high speed steel HS6-5-2 amounting 1100 HV0,065 was achieved by using the amperage of electric arc of 50 A. The overlapping of remeltings is connected with the possibility of occurence of the microhardness decrease in the area of overlapping of the heat influence zone of second remelting (another remelting) on the first remelting (the previous one).
Authors and Affiliations
A. Dziedzic
Keywords
Related Articles
- EP ID EP72289
- DOI -
- Views 123
- Downloads 0
Synthesis of sequential control algorithms for pneumatic drives controlled by monostable valves
Application of the Grafpol method [1] for synthesising sequential control algorithms for pneumatic drives controlled by monostable valves is presented. The developed principles simplify the MTS method of programming prod...
Predicting ADI mechanical properties
Ductile cast iron was quench-hardened with the isothermal transformation according to two alternatives. The first treatment alternative consisted in the austenitizing process at temperature t = 830, 860 i 900°C and anne...
Efficiency of protective coatings on high creep resistant cast steel
This paper presents results of research of multilayer aluminium–silicon coatings. Aluminium–silicon coatings were created on high– temperature creep resist cast iron using slurry method in air atmosphere. These coatings...
Measurement of large-size casting geometry of the CMM
The aim of this paper is to present the geometric dimensions’ control of large castings and moulds on coordinate measuring machines (CMMs). Precise measurements of large components are connected with many problems that a...
Abrasive wear resistance of high-vanadium cast iron
The study presents the results of tribological tests made on Fe-C-V and Fe-C-V-Si alloys undergoing volume solidification and containing carbon in a range of 1,43-2,58%, vanadium in a range of 5,34-14,77%, and silicon in...