The Influence of Speed Cooling on Some Properties of Laminated Steel
Journal Title: Analele Universitatii "Dunarea de Jos" din Galati. Fascicula IX, Metalurgie si Stiinta Materialelor - Year 2016, Vol 39, Issue 1
Abstract
This study presents a possibility to predict the connection between the cooling regime and the properties of steel. An important factor to enhance the properties of steel is the speed of the cooling regime. To be in accordance with the experimental results, this study considered a correlation between the speed of cooling for laminated steel with a low carbon content and other properties of steel. It is important to choose the optimal cooling regime because the steel was laminated at high temperature.
Authors and Affiliations
Carmen Penelopi PAPADATU, Marian BORDEI
Keywords
Related Articles
- EP ID EP580996
- DOI -
- Views 77
- Downloads 0
Behaviour at Nitriding in Fluidized Layer of Austenitic Stainless Steels at the Temperature of 1050 °C
Nitriding at low temperatures, 450-500 oC of austenic stainless steels lead to the obtaining of the tough layers over 1000 HV005 but having thicknesses of tenths of microns. Moreover, nitriding at 500ºC has determined th...
Low Potential Heat Recovery Using Heat Pumps
This paper presents a study on the possibility of recovering low thermal potential heat from the cooling technological water of industrial processes. The analysed solution consists in the use of a heat pump which would s...
Analysis Tools for Sustainable Management of Cell Phone Waste for Metals Recovery
A modern cell phone contains over 60 metals, combined physically or chemically and in some cases covered with various types of plastics, ceramics, etc. For recycling, each metal from the device needs to be analyzed indiv...
Hardening of the Grey Cast Iron through the Vibrating Electrode Method Using a WC Electrode and in Combination with TiC and Ti Electrode
There have been tested samples of grey cast iron, the hardening being made through WC coating through the vibrating electrode method with a layer, two layers and through double layers combined with Ti and TiC. Besides do...
Mechanical and Laser Cladding of High-Speed Steel on a Steel Support
Multilayer cladding by injection of high-speed steel powder with 0.82%C, 4.7%Mo, 6.4%W, 4.1%Cr, 2.02%V, 0.3%Mn, as chemical composition, in melted bath by CO2 continuous wave laser connected to x-y-z coordinate table was...