The Lithium Power Sources Based on Porous Carbon Material
Journal Title: Фізика і хімія твердого тіла - Year 2015, Vol 16, Issue 1
Abstract
The paper describes the use of porous carbon material (PCM), obtained from plant raw materials as anode of lithium power source (LPS). It is established that the electrochemical parameters of LPS at current density of C/20 are stable over long cycling (over 90 charge/discharge cycles) – discharge capacity remained at 150 mA•h/g, and Coulomb efficiency exceeds 95%.
Authors and Affiliations
V. I. Mandzyuk, V. G. Khomenko, V. M. Sachko, I. F. Myronyuk, V. Z. Barsukov
Keywords
Related Articles
- EP ID EP313928
- DOI 10.15330/pcss.16.1.217-220
- Views 41
- Downloads 0
Formation of the Sputtered Phase of PbTe Crystals by Ar+ Plasma and Re-deposition of the Sputtered Species at Secondary Neutral Mass Spectrometry Conditions
Formation of the Pb and Te sputtered phase under exposure of the lateral surface of PbTe crystals grown from melt by the Bridgman method by Ar+ plasma at Secondary Neutral Mass Spectrometry (SNMS) conditions and re-depos...
Symmetrical Analysis Phonon Modes of Crystal b-Ag8SnSe6
Symmetrical analysis of the phonon spectra of lowtemperature b-phase of crystal Ag8SnSe6 carried out. At the room temperature argyrodite Ag8SnSe6 belong to orthorhombic system with space group symmetry Pmn21. Classificat...
Properties and Practical Application of Nanoporous Silicate Matrices, Filled withMixture of NaNO2 and BaTiO3 Ferroelectrics. influence of Co- Encapsulation
Results of research the characteristics of MCM-41 porous silica matrix, encapsulated into her pores bysodium nitrite and its mix with barium titanate were presented. Nature of changes the impedance frequencydispersion, e...
Electrical transport properties of R3Ag4Sn4 compounds (R = Gd, Tb, Dy, Ho)
Electrical transport properties of the R3Ag4Sn4 (R = Gd, Tb, Dy, Ho) intermetallics crystallized in the orthorhombic Gd3Cu4Ge4 structure type (space group Immm) were studied in the temperature interval 11-300 K. Measurem...
Investigation of Changes in Resistivity of n Si with Temperature and Uniaxial Stress
In this work the changes in resistivity of n Si with temperature and uniaxial stress X, oriented both in <100> and in [111] direction, were investigated. The value of the anisotropy parameter of mobility was obtained in...