The Peculiarities of Refractory Phases in the System Al-Сr2О3-B2O3
Journal Title: Фізика і хімія твердого тіла - Year 2014, Vol 15, Issue 4
Abstract
In this paper we investigated the temperature and time dependence of Education refractory Al2O3 phases during the synthesis reaction at temperatures of isothermal holding from 1000°C to 1600°C and a duration of 2 to 16 minutes. It is shown that the synthesis reaction of Al-Cr2O3 and Al-B2O3 occurs in several stages and leads to the formation of additional, on fusible phases such as B2O3, chromium metal and aluminum and chromium yntermetalidiv that at a high temperature sintering decay modes to form refractory compounds. Using the reaction mixture Al-Cr2O3 -B2O3 ( energy yield of the reaction is 730 kJ, allowing at temperatures from 1300°C to obtain formulations contain only refractory ceramic phase.
Authors and Affiliations
O. A. Sivak, M. I. Cherednyk, I. M. Totskiy, A. Yu. Popov, V. A. Makara
Keywords
Related Articles
- EP ID EP317420
- DOI -
- Views 41
- Downloads 0
Thermoelectric Efficiency of Solid Solutions PbTe1-xSex Over a Wide Temperature 300-800 K
The results of research of kinetic parameters (mobility, coefficients thermo power, electrical conductivity and thermal conductivity) samples PbTe1-xSex with different composition х = 0; 0,5; 0,15 та 0,25 produced sinter...
Features of Time Characteristics of Diffusion Properties of Polymer Modified Film Materials for Technical Application
The changes of the oxygen permeability of packings from polymeric film materials intended for prolonged storage of metal products have been investigated. High indexes of initial oxygen permeability were recorded due to i...
Correlation of Antiwear and Antifriction Properties of Carbon Fiber with Hardness and Roughness of Metal Adjacent Surfaces
Correlations between friction coefficient and intensity of wear of polytetrafluoroethylene – carbon-plastic, derived by CMA-technology, and nature, hardness, roughness (initial and the one that arose in the friction and...
Synthesis, Crystal Chemistry and Antistructure Modelling of CoFe2O4 Nanoparticles Prepared by Citrate Sol-Gel Method
Cobalt ferrite nanoparticles were synthesized by the citrate sol-gel method and characterized by XRD, FT-IR, TG-DSC techniques. X-ray analysis confirms the formation of single phase cubic partially inverse spinel structu...
Strength of the Carbon Nanotube Films
The strength of nanodevices is caused by the interatomic distance decreace in nanostructures.Graphene nanofilm has 35 times larger strength than the steel. Thin whisker crystals grown from the gas phase are ten times mor...