The possibility of using filamentous fungus in the technology of the formation of highly porous surfaces on biocompatible substances
Journal Title: Поверхня - Year 2018, Vol 25, Issue 10
Abstract
This work reports the possibility of using fungal mycelium to form the highly porous surfaces of biocompatible substances by the example of calcium acetate. The main aim of the work was the search of conditions for forming of porous structures from the volatile molecules of calcium acetate on microscopic filaments of fungal mycelium and the study of the surfaces formed from calcium acetate. Highly porous surfaces were formed by the condensation of volatile calcium acetate molecules on the fungal mycelium during vegetative development under condition close to room temperature. Various conditions allow the mean pore size of the surface of calcium acetate to range from 25÷50 μm. Experiment shows that the using of the natural structure of fungal mycelium as the filamentous substratum for condensation of the solid highly porous formations of calcium acetate can change the porousness of our samples and vary the use of these biocompatible materials in different spheres.
Authors and Affiliations
M. O. Vorobets, V. V. Strebezhev
Keywords
Related Articles
- EP ID EP463590
- DOI 10.15407/Surface.2018.10.137
- Views 99
- Downloads 0
Пористая структура порошков наноразмерного боразографена
Исследованы структурные особенности порошков наноразмерного боразографену (t-BNg.). Результаты показали, что в процессе очистки порошок t-BNg становится микро-, мезопористым (монодисперсным) с узким распределением мезопо...
Elementary acts of the reaction of molecular oxygen recovery over nitrogen-doped sp2-carbon cluster: quantum chemical study
Density functional theory (B3LYP, 6-31 G**) was used to calculate the spatial and electronic structure of the oxygen molecule complexes with the coronene molecule and its nitrogen-containing analog, where two nitrogen at...
Синтез і адсорбційні властивості кобальт-вуглецевого нанокомпозиту на основі лушпиння соняшнику
Просочення лушпиння насіння соняшнику хлоридом кобальту з подальшим піролізом при 800 °С в атмосфері аргону дозволяє отримати метал-вуглецевий магніточутливий наноком-позит з розвиненою мікропористістю. Використання дани...
Porous structure of nano-dimensional boraso-graphenic powders
The structural features of surface of the nano-dimensional bor-azo-graphenic powders (t-BNg) after previous washing in boiling water were researched. The results showed that after process of purifier (washing) the powder...
Вплив атомів нітрогену і бору, впроваджених в графеноподібну матрицю, на адсорбцію молекулярного водню
Методами квантової хімії (ТФГ, B3LYP, 6-31G**) досліджені закономірності взаємодії молекул водню з графеноподібними площинами, в яких два атоми Карбону заміщені атомами Нітрогену, чи Бору. Для врахування дисперсійних вне...