Weld microstructure in cast AlSi9/SiC(p) metal matrix composites
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2
Abstract
Welded joint in cast AlSi9/SiC/20(p) metal matrix composite by manual TIG arc welding using AlMg5 filler metal has been described in his paper. Cooling curves have been stated, and the influence in distribution of reinforced particles on crystallization and weld microstructure. Welded joint mechanical properties have been determined: hardness and tensile.
Authors and Affiliations
J. Wysocki, K. Gawdzińska, S. Lenart
Keywords
Related Articles
- EP ID EP71679
- DOI -
- Views 135
- Downloads 0
Analysis of the influence oxygen and hydrogen during melting aluminium and his alloys
In the work was stated term the analysis of ion influences in melting codnuction of aluminium and his alloys. Influence from hydrogen and oxygen, hydrogen and oxygen and steam water together was distinguished. Where have...
The Dependence of Castings Quality Produced in Clay Moulding Mixtures from the Properties of Binder Based on a Montmorillonite
Casting quality depends on many factors including the quality of the input materials, technology, material securing and last but not least, the mould into which the casting is casted. By pouring into a single-shot mould,...
Heat-insulating moulding sand with the glycol addition
The article presents a selection of the composition and basic properties of highly insulating moulding sand. Sandmix is designed especially for thin-walled castings with high tendency to oxidation - particularly in spati...
The Decreasing of Die Cracking for HDPC Technology by Changing Parameters of Heat Treatment
In earlier works were described trends in the production of tools for die casting (hot work). Almost the entire set of issues dealt with may seem insignificant when incompletely assembled acceptance of the material and t...
Influence of the technology of melting and inoculation preliminary alloy AlBe5 on change of concentration of Al and microstructure of the bronze CuAl10Ni5Fe4
Examining was the aim of the work: influence of the permanent temperature 1300°C ± 15°C and changing time of isothermal holding in the range 0÷50 minutes on the melting loss of aluminum in the bronze CuAl10Ni5Fe4; the qu...