A continuous net-like eutectic structure enhances the corrosion resistance of Mg alloys
Journal Title: International Journal of Bioprinting - Year 2019, Vol 5, Issue 2
Abstract
Mg alloys degrade rather rapidly in a physiological environment, although they have good biocompatibility and favorable mechanical properties. In this study, Ti was introduced into AZ61 alloy fabricated by selective laser melting, aiming to improve the corrosion resistance. Results indicated that Ti promoted the formation of Al-enriched eutectic α phase and reduced the formation of β-Mg17Al12 phase. With Ti content reaching to 0.5 wt.%, the Al-enriched eutectic α phase constructed a continuous net-like structure along the grain boundaries, which could act as a barrier to prevent the Mg matrix from corrosion progression. On the other hand, the Al-enriched eutectic α phase was less cathodic than β-Mg17Al12 phase in AZ61, thus alleviating the corrosion progress due to the decreased potential difference. As a consequence, the degradation rate dramatically decreased from 0.74 to 0.24 mg·cm-2·d-1. Meanwhile, the compressive strength and microhardness were increased by 59.4% and 15.6%, respectively. Moreover, the Ti-contained AZ61 alloy exhibited improved cytocompatibility. It was suggested that Ti-contained AZ61 alloy was a promising material for bone implants application.
Authors and Affiliations
Cijun Shuai, Wenjing Yang, Youwen Yang, Chengde Gao, Chongxian He, Hao Pan
Keywords
Related Articles
- EP ID EP678707
- DOI -
- Views 184
- Downloads 0
The mussel-inspired assisted apatite mineralized on PolyJet material for artificial bone scaffold
With the development of three-dimensional (3D) printing, many commercial 3D printing materials have been applied in the fields of biomedicine and medical. MED610 is a clear, biocompatible PolyJet material that is medical...
Roles of support materials in 3D bioprinting – Present and future
Bioprinting has been introduced as a new technique in tissue engineering for more than a decade. However, characteristics of bioprinted part are still distinct from native human tissue and organ in terms of both shape fi...
Printing amphotericin B on microneedles using matrixassisted pulsed laser evaporation
Transdermal delivery of amphotericin B, a pharmacological agent with activity against fungi and parasitic protozoa, is a challenge since amphotericin B exhibits poor solubility in aqueous solutions at physiologic pH valu...
Artificial vascularized scaffolds for 3D-tissue regeneration — a report of the ArtiVasc 3D Project
The aim of this paper is to raise awareness of the ArtiVasc 3D project and its findings. Vascularization is one of the most important and highly challenging issues in the development of soft tissue. It is necessary to su...
Concentric bioprinting of alginate-based tubular constructs using multi-nozzle extrusion-based technique
Bioprinting is a layer-by-layer additive fabrication technique for making three-dimensional (3D) tissue and organ constructs using biological products. The capability to fabricate 3D tubular structure in free-form or ver...