A SIMPLE AND EFFECTIVE ROUTE FOR PREPARATION OF POLYSTYRENE(PS) NANOSPHERE CONTAINING CDSE QUANTUM DOTS BY ELECTROSPINNING
Journal Title: Topics in Chemical & Material Engineering (TCME) - Year 2018, Vol 1, Issue 1
Abstract
Fluorescent CdSe quantum dots (QDs) were dispersed into polystyrene (PS) nanospheres by electrospinning a CdSe/PS blent solution. In the process, assembled quantum dots did not take place, quantum dots were uniformly dispersed in the polymer matrix which were either single-colored or double-colored nanospheres. The morphology and distribution of composite nanospheres were characterized by field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM).The diameter of the composite nanospheres is reduced from 1150nm of a pure PS nanosphere to about 570nm with the increased amount of CdSe QDs. The photoluminescence (PL) spectral analysis indicates that the peak position of CdSe QDs composite nanospheres in either solid state or water is identical to that of CdSe/PS blending solution, at about 587nm and 611nm.especially the interference possibility of two peaks in double-colored system is avoided. And the position is still unchangeable when they are left for at least one month, indicating the stable photoluminescent property of the fluorescent composite nanospheres
Authors and Affiliations
Song Yan, Wang Fang-Fei
Keywords
Related Articles
- EP ID EP414493
- DOI 10.26480/icnmim.01.2018.213.215
- Views 56
- Downloads 0
RECOGNITION METHOD OF POWER QUALITY DISTURBANCE SIGNALS BASE D ON IMAGE FEATURES
In order to meet the requirements of power quality monitoring and grid active control of distributed generation, in this paper, a new method to identify power quality transient disturbances by digital image processing is...
PRELIMINARY STUDY ON IMMOBILIZATION TECHNOLOGY OF TIO2 PHOTO CATALYST
TiO2 was used as photo catalyst to treat organic effluent firstly. Methyl orange solution was utilized as simulated wastewater for optimizing conditions of the reaction. That is: reaction time as 60min, solution concentr...
CONTROL ON PRODUCTION COST AND QUALITY OF CARBON FIBRE PRECURSOR
In the production of carbon fibre industry, oiling of carbon fibre precursor can impart fibre smoothness, antistatic property, and bundling property, and also allows the precursors to have sufficient high temperature res...
CORN COB POLYMER FLOCCULANT PREPARATION METHOD AND ITS APPLICATION IN ORGANIC WASTE WATER TREATMENT
In this paper, the corn cob was modified to prepare cellulose xanthogen with flocculation. A comparative experiment was conducted on the flocculating adsorption effect of the finished product. Experiments show the best e...
EFFECT OF MEA HOT-PRESSING ON THE PERFORMANCE OF DIRECT METHAN OL FUEL CELLS
MEA based on Nafion 115 has been prepared with GDL-based method for direct methanol fuel cell applications. The results of unit cell tests show that different temperature and pressure of hot-pressing during MEA preparati...