Acid Aging Effects on Surfaces of PTFE Gaskets Investigated by Thermal Analysis
Journal Title: Tribology in Industry - Year 2016, Vol 38, Issue 4
Abstract
This paper investigates the effect of a prolonged acid attack on the surface of PTFE by Thermogravimetric Analysis (TGA) and Differential Scanning Calorimetry (DSC). PTFE is very non-reactive, partly because of the strength of carbon?fluorine bonds and for its high crystallinity, and, as a consequence, it is often used in containers and pipework with reactive and corrosive chemicals. The PTFE under analysis is commercialized by two alternative producers in form of Teflon tapes. These tapes are adopted, as gaskets, in process plants where tires moulds are cleaned by acid solutions inside a multistage ultrasonic process. In this case, PTFE shows, in a relatively short operation time, inexplicably phenomena of surface degradation, which could be related, in general terms, to an acid attack. But, even considering the combined effect of ultrasonic waves, temperature, humidity and acid attack, the PTFE properties of resistance nominally exclude the risk of the extreme erosion phenomena as observed. The present experimental research aim at investigating this contradiction. A possible explanation could be related to the presence in the cleaning solution of unexpected fluorides, able to produce fluorinating agents and, thus, degrade carbon-fluorine bonds. Considering more the 300 chemical elements a tire compound consists in, it is really complex to preserve the original chemical composition of the cleaning solution. In this research PTFE samples have been treated with different mixtures of acids with the aim at investigating the different aging effects. The thermal analysis has permitted the experimental characterization of PTFE surface properties after acid attack, providing evidence of the degradation phenomena. In particular, the different acid treatments adopted for accelerating the aging of gaskets have highlighted the different behaviour of the PTFE matrix, but also differences between manufacturers.
Authors and Affiliations
Cristiano Fragassa, L. Giorgini, Ana Pavlovic, G . Zattini
Keywords
Related Articles
- EP ID EP228376
- DOI -
- Views 91
- Downloads 0
Reduction and Maintance of Turbochargers by Applying Valid Tribological Constructing
Condition recordings and turbochargers test results indicate that during the long driving at higher speeds may cause turbochargers overheat. Lubricate termination after shutting generator can cause damage to the sliding...
Simulation of Anti Wear Performance Using a Modified Brugger Test Set Up
Modern hydraulic oils have to fulfill a broad variety of parameters limitations to guarantee a proper system performance throughout a considerable lifetime. A comprehensive test of the liquids nowadays just can be perfor...
The Influence of Corrosion on the Microstructure of Thermally Treated ZA27/SiCp Composites
The influence of corrosion on the microstructure of ZA27/SiCp composites was examined. The composites were produced by compo casting technique and then subjected to the thermal treatment (T4 regime). Microstructural exam...
Carbide Type Influence on Tribological Properties of Hard Faced Steel Layer – Part I – Theoretical Considerations
This paper gives a theoretical review of influence of the most important alloying elements on steel, and review of the most important carbide-forming elements and states the conditions which elements should fulfill in or...
Fabrication of LM25/SiO2 Metal Matrix Composite and Optimization of Wear Process Parameters Using Design of Experiment
LM25 aluminium alloy reinforced with 15 wt% SiO2 metal matrix composite was fabricated by liquid metallurgy technique. Microstructure of the fabricated composite specimen was observed using inverted metallurgical microsc...