Analysis of the austenitic stainless steel's r-value behavior at elevated temperatures
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2015, Vol 22, Issue 2
Abstract
An analysis of the anisotropy properties of austenitic steel AISI 304 (X5CrNi18-10) at elevated temperatures is presented in this paper. Considerations of the anisotropy problems are presented in the theoretical part of the paper, as well as the procedure for determination of the normal anisotropy coefficient. The experimental part of the paper describes the plan, methodology and equipment for testing of material's normal anisotropy and mechanical characteristics. The objective of conducting the experiments was to investigate influence of temperature on normal anisotropy, as well as on the mechanical properties of the considered material. The normal anisotropy was monitored by the coefficient – the so-called "r-value". Besides that, the tensile strength, yield stress and elongation at break were monitored, also. The tests were done on the 0.7 mm thick sheet metal within the temperature range 20 to 700 °C.
Authors and Affiliations
Dušan Arsić, Milan Djordjević, Srbislav Alexandrović, Vukić Lazić, Ružica Nikolić, Branislav Hadzima
Keywords
Related Articles
- EP ID EP148123
- DOI -
- Views 112
- Downloads 0
The investigation of the corrosion resistance of the tension clamps Skl14
At the level crossings it is possible to find the problems with the corrosion of the parts of the fastening system. These problems are especially at the rubber level crossings and in the tunnels. As a part of the thesis...
STUDY OF CALCIUM PHOSPHATE (DCPD) ELECTRODEPOSITION PROCESS ON THE Mg-3Al-1Zn MAGNESIUM ALLOY SURFACE
Evaluation of calcium phosphating process realized on the Mg-3Al-1Zn alloy surface after grinding was investigated by electrochemical tests supported by photodocumentation. The electrodeposition treatment was performed b...
MICROSTRUCTURE EVOLUTION OF PURE TITANIUM DURING ECAP
The main goal of the presented paper was to describe deformation behaviour of the commercial purity titanium during the ECAP method. Attention was paid particularly on reached mechanical properties of above mentioned mat...
Effects of Tribological Parameters on Slurry Erosion Behaviour of Uncoated and Coated Materials: A Review
This paper describes the pioneering work of various researchers in the field of slurry erosion behaviour of uncoated and coated materials in various industrial applications. The present study is focused on the slurry ero...
THE EFFECT OF THE ANNEALING TEMPERATURE ON THE CORROSION RESISTANCE OF WELD JOINT OF AISI 310 STEEL - SHORT COMMUNICATION
The article presents samples of weld joint of AISI 310 austenitic steel which were subjected to solution annealing at various temperature - time exposures. The objective of the experiment was to determine the annealin...