Application of the method of thermo-power in diagnosing fatigue strength and intergrain corrosion
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2
Abstract
In area of flat defect, predefined a gradient tireless - corrosive tensions, a double electric layer, conditioned the spatial redistribution of electronic closeness, is formed. It shows up a local rejection mikro-thermo-power at use of heating edge of tungsten thermocouple. Test approbation of method is conducted on the deformed chromel.
Authors and Affiliations
V. J. Prokhorenko, S. V. Prokhorenko, P. M. Koval, T. I. Dominjuk
Keywords
Related Articles
- EP ID EP71695
- DOI -
- Views 72
- Downloads 0
The structure of Ni–enriched Al–Ni molten alloy before solidification
The structure of Ni–based molten alloy, containing 88,02w.%Ni and dopped both with Zr (0,46w.%) and B (0,02w.%) has been studied by means of X–ray diffraction method at temperature 1500 K. Structure factor and pair corre...
Experimental stand for melting and casting of ultralight Mg-Li alloys
The article presents the design guidelines and technical implementation of an experimental stand for melting and casting in controlled protective atmosphere the ultralight magnesium-lithium alloys, including also a small...
Fatigue strength of MAR-M509 alloy with structure refined by rapid crystallization
This study presents test results of high-cycle (N>2⋅107) fatigue bending strength of MAR-M-509 cobalt alloy samples, as cast and after surface refining with a concentrated stream of heat. Tests were conducted on samples...
Effect of pouring temperature on the Lost Foam Process
In this study, the analysis of the influence of the pouring temperature on manufacture process of castings by the Lost Foam method was introduced. In particular, numerical simulation results of effect of silumin and grey...
Crystallisation and microstructure of low-silicon silumins with alloy additions
The paper presents the results of the analysis of crystallisation and microstructure of non-alloy silumins that contain: 2,0÷6,0% of Si and alloy additions, approximately: 4,0% Ni, 4,0% of Cu and 0,5% of Mg, the knowledg...