Chemical and Structural Changes for Bimetallic Materials Obtained by the Welding Process
Journal Title: Analele Universitatii "Dunarea de Jos" din Galati. Fascicula IX, Metalurgie si Stiinta Materialelor - Year 2005, Vol 28, Issue 2
Abstract
This paper presents the transformations which take place during the obtaining process of bimetallic materials. As a plating process was used the welding. The added material was a bronze with aluminum complex alloyed with iron, nickel. The based material was the steel. EDAX analyses and microstructures analyses were done in order to explain the metallurgical processes which take place during the facing by melting.
Authors and Affiliations
Anişoara CIOCAN, Felicia BRATU
Keywords
Related Articles
- EP ID EP664226
- DOI -
- Views 68
- Downloads 0
Corrosion Behavior of Some Materials in 0.5M Ammonium Hydroxide Solution
The present work has the purpose of studying metallographic aspects and corrosion resistance of three materials used in ammonia stripping plants. The corrosion process was evaluated by gravimetric tests and potentiodynam...
Elastic Modulus of Coatings by Pendulum Impact Test
The pendulum impact scratch device with high precision system in measuring normal and tangential forces during scratching has been used to study elastic modulus of coatings. The criterion for evaluation of elastic modulu...
Dust Emissions from an Integrated Steel Mill in Correlation with Human Exposure and their Adverse Health Effects
Many of the metallurgical operations contribute to generation of the dust emissions if these are not properly controlled and managed. The relevant sectors as important sources for airborne dust are: coke oven plant, sint...
Influence of Technological Parameters on the Evolution of Nickel Films Deposited by Electrolysis
The influence of technological parameters on the structure of nickel layers electrodeposited on a copper substrate in a Watts bath has been studied. The complex influence of current densities, temperature and pH values o...
Laser Surface Alloying of Some Steels from SiC Predeposited Powders
For the purpose of studying the possibilities of increasing the wear resistance, specimens of three steels with 0.2%C, 0.46%C and 1%C were surface alloyed with reinforcement from overlapping pastes with green SiC hard pa...