Edge Absorption of (Y0.06Ga0.94)2O3 Thin Films
Journal Title: Фізика і хімія твердого тіла - Year 2017, Vol 18, Issue 1
Abstract
Fundamental absorption edge of (Y0.06Ga0.94)2O3 thin films, obtained by radio-frequency ion-plasmous sputtering, was investigated using the method of optical spectroscopy. It was established that these films are formed in the monoclinic structure of β-Ga2O3. The optical band gap of these films is greater than β-Ga2O3 films and is 4.66 eB for films annealed in oxygen atmosphere, 4.77 eV for the films annealed in argon atmosphere and 4.87 eV for the films, restored in a hydrogen atmosphere. Consolidated effective mass of free charge carriers in (Y0.06Ga0.94)2O3 films after annealing and after reconstitution in hydrogen was estimated. It was found that the concentration of charge carriers after annealing in oxygen atmosphere is 1.32×1018 cm-3, after annealing in argon atmosphere - 3.41×1018 cm-3 and after reconstitution in hydrogen is 5.20×1018cm-3, which is typical for degenerated semiconductors. It was shown that the shift of fundamental absorption edge in (Y0.06Ga0.94)2O3 thin films is caused by Burstein-Moss effect.
Authors and Affiliations
O. M. Bordun, I. Yo. Kukharskyy, I. I. Medvid, Zh. Ya. Tsapovska
Keywords
Related Articles
- EP ID EP263679
- DOI 10.15330/pcss.18.1.89-93
- Views 62
- Downloads 0
Isothermal section of the Ho–Cu–Sn ternary system at 670 K
The interaction of the components in the Ho-Cu-Sn ternary system was investigated at 670 K over the whole concentration range using X-ray diffraction and EPM analyses. Four ternary compounds were formed in the Ho–Cu–Sn s...
Methods of Heat Capacity Measurements of Crystal (Review)
The analysis of the basic methods of heat capacity measurements of solids and construction schemes of devices for implementation these techniques have been shown. The general theoretical and empirical formulas allow to q...
Tribosurface Properties of Polymer Composite in Friction and Wear on Anisotropic Rough Surface of Steel 45
Regularities of change of anisotropic roughness surfaces of steel 45 in friction and wear in a pair with polymer composite has been researched. It has been detected that the topography of the conjugated metal surface wit...
Short Range Order Change at Structural Relaxation in Fe75Si6B14Mo5 Amorphous Alloy
Structural relaxation process in Fe75Si6B14Mo5 amorphous alloy has been studied by means of X-ray diffraction method. Structure parameters, obtained from analysis of structure factors and pair correlation functions are u...
Desorption Mas Spectrometry Stady of Shungite
Mass spectrometric methods TPD-MS, LDI-ToF was staded shungite and its water, ethanol and toluene extracts obtained under ultrasound irradiation. The presence of fullerene C60 in aqueous and ethanol extracts of shungite...