Effect of Microstructure on the Compressive Mechanical Properties of Ti-20Zr-6.5Al-4V Alloy
Journal Title: Materials Science-Medžiagotyra - Year 2019, Vol 25, Issue 1
Abstract
The effect of microstructure on the mechanical properties of Ti-20Zr-6.5Al-4V alloy after solution and aging treatment was investigated by compression tests. The results showed that the microstructure was consisted of a duplex phase αʺ + β structure after solution treatment. With increasing solution treatment temperature, the size of β phase grain increased and the amount of αʺ phase decreased. The ultimate compressive strength and elongation decreased with increasing solution treatment temperature, while the yield strength increased. After aging-treatment at 700 ºC for 1.5 h, the microstructure consisted of a large amount of globular α phase, a little amount of fine acicular α phase and bulk β phase for the samples solution-treated at 850 ºC for 0.5 h. With increasing initial solution treatment temperature, the amount of globular α phase and bulk β phase decreased, however, the amount and size of acicular α phase increased after aging treatment. The ultimate compressive strength and elongation decreased with increasing initial solution treatment temperature, whereas the yield strength firstly increased, and then slightly decreased.
Authors and Affiliations
Yuanbiao TAN, Jingli DUAN, Wenchang LIU, Song XIANG, Fei ZHAO, Yilong LIANG
Keywords
Related Articles
- EP ID EP452515
- DOI 10.5755/j01.ms.25.1.18737
- Views 65
- Downloads 0
Electrochemical and Tribological Properties of TiSiCN Coatings in Coolant
TiSiCN coatings were prepared using DC and RF magnetron co-sputtering system. The influence of target powers on phase structures, mechanical properties, tribological and electrochemical properties were studied. The resul...
Fabrication and Characterization of Graphene/Epoxy Nanocomposites
Graphene with high electric and thermal conductivities has been widely used as reinforced filler. In this study, graphene loadings in the range between 0.3 and 1.0 wt.% were added to the epoxy to fabricate the nanocompos...
Enhanced Magnetic Squareness in Manganese-Bismuth Mechanical Alloys Incorporating Magnesium Oxide
Manganese-bismuth (MnBi) mechanical alloys have been under development for novel permanent magnets without rare-earth elements. The ball-milling of bismuth (III) oxide and manganese powders in this work leads to soft mag...
Comparative Study on the Tribological Properties of AISI52100 Steel Surface Modified by Graphite/MoS2 Composite Coating and Manganese Phosphate Coating
Surface modification is an important method to improve the contact fatigue life of transmission parts. The preparation of high performance coating with good tribological properties on the gears and bearings has become th...
Multi-response Optimization of End Milling Parameters for Al-Zn-Mg/SiC Co-continuous Composite Using Response Surface Methodology
A co-continuous ceramic composite (C4) was manufactured by gravity infiltration. The effect of varying machining parameters namely, speed, feed and depth of cut during end milling of C4, on the multi-responses of surface...