EFFECT OF PLASTICIZERS ON WORKABILITY AND COMPRESSIVE STRENGTH OF CONCRETE

Abstract

Worldwide, a great deal of research is currently being conducted concerning the use of plasticizers in increasing the workability and strengthening of reinforced cement concrete and plain cement concrete members. Use of plasticizer application is a very effective way to increase workability, decreasing the water cement ratio and finally increasing the compressive strength of concrete. First of all in this thesis work literature review based on workability and compressive strength of concrete as experimental investigations are studied and need of the study is included. In the first phase of the study concrete mix design pr ocedure is adopted for M30 and M35 grade of concrete. For the determination of mix design various properties of concrete ingradients is conducted in the laboratory and results are recorded. In the second phase two sets of concrete cubes were casted for thi s experimental test program. In set A 36 cubes were casted of M30 grade out of which 18 cubes are made with keeping water cement ratio as 0.4 and remaining 18 cubes are made with keeping water cement ratio as 0.5 with variations in the amount of plasticize rs. In set B again 36 cubes were casted of M35 grade out of which 18 cubes are made with keeping water cement ratio as 0.4 and remaining 18 cubes are made with keeping water cement ratio as 0.5 with variations in the amount of plasticizers. Lastly the cube s are tested for Workability and Compressive strength using slump cone test apparatus and compression testing machine. Effect on workability and strength with variation in the dosage of plasticizers are studied from experimental data obtained for 7 days an d 28 days. Finally it has been concluded that use of plasticizers as admixtures results in improvement in workability and finally an increase in compressive strength of concrete. This leads to a step ahead in durability of the concrete and in turn is a du rability of the structure

Authors and Affiliations

Yogesh Sharma*

Keywords

Related Articles

 MOSAICING IN VARIOUS IMAGES: A SURVEY

 K-means clustering and watershed are the key techniques used as a combination, Edge detection procedure and region, merging are also used. Merging method based on mean gray values and edge strengths (T1, T2) are u...

 Improving Performance of KNN Algorithm by Using Enhanced CBIR Techniques for Retrieval of MRI Images

 CBIR (Content Based Image Retrieval) is a method utilized for the recovery of coveted pictures from a huge collection of pictures in a database on the premise of picture characteristics, for example, coloration, s...

 FAULT DIAGNOSIS OF MEMORIES USING BIST AND ITS RELIABILITY

[sub][/sub] New memory technologies and processes introduce new defects that cause previously unknown faults. Dynamic faults are among these new faults; they can take place in the absence of the traditional static f...

 OPTIMIZATION OF PEELING TIME AND OPERATIONAL SPEED FOR CASSAVA PEELING USING CENTRAL COMPOSITE DESIGN AND RESPONSE SURFACE METHODOLOGY

 The effect of two process parameters namely: peeling time and operational speed on the peeling process of cassava during cassava processing were investigated. The optimization of flesh loss from cassava was ca...

 THE PRODUCTION OF BIODIESEL BY TRANSESTERIFICATION PROCESS OF SUNFLOWER OILS AND ETHANOL, USING ALKALI CATALYST

 The transesterification reaction of sunflower oil with ethanol in presence of alkaline catalyst sodium hydroxide was studied. The effect of mass ratio of ethanol to oil, the mass ratio of catalyst to oil and react...

Download PDF file
  • EP ID EP153329
  • DOI -
  • Views 78
  • Downloads 0

How To Cite

Yogesh Sharma* (30). EFFECT OF PLASTICIZERS ON WORKABILITY AND COMPRESSIVE STRENGTH OF CONCRETE. International Journal of Engineering Sciences & Research Technology, 4(7), 812-820. https://europub.co.uk/articles/-A-153329