Electrodeposition Obtaining and Corrosion Behaviour of Phenol Formaldehyde Resin/Zinc Composite Coatings
Journal Title: Analele Universitatii "Dunarea de Jos" din Galati. Fascicula IX, Metalurgie si Stiinta Materialelor - Year 2008, Vol 31, Issue 2
Abstract
The present work has the purpose of obtaining composite coatings in zinc matrix by using phenol - formaldehyde resin type NOVOLAC (RESITAL 6358/1) in the electrodeposition process of zinc. The PF resin/Zn composite coatings were electrodeposited from a suspension of PF resin particles (diameter < 56 μm) in aqueous zinc sulphate electrolyte. Suspension was prepared by adding 10 g/L and 25 g/L PF resin particles into solution. The pure zinc coating has a rather regular surface, whereas the composite coatings surface has fine surface structure. For layers obtained at 3A/dm2 the polarization resistance is higher for composite coatings with 10 g/L PF resin (Rp = 238.75 Ω cm2 ) than pure zinc (Rp = 34.54 Ω cm2). For layers obtained at 5A/dm2 the polarization resistance is higher for composite coatings with 25 g/L PF resin (Rp = 430.19 Ω cm2) than pure zinc (Rp = 127.34Ω cm2). As test solution 0.5M sodium chloride was used, it was observed that by adding PF resin particles in zinc electrolyte for electrodeposition it was obtained a very good distribution of resin particles on zinc surface and PF resin/Zn composite coatings obtained are most resistant at corrosive attack than pure zinc obtained from electrodeposition under the same conditions.
Authors and Affiliations
Olga MITOŞERIU, Alina CIUBOTARIU, Lidia BENEA, Pierre PONTHIAUX, Francois WENGER
Keywords
Related Articles
- EP ID EP659460
- DOI -
- Views 49
- Downloads 0
Nanostructured Surface for 38MoCrAl09 Steel by Nitriding in Nitrogen Atmosphere and YAG:Nd Pulse Laser Activation
YAG:Nd pulse laser is usually used for cutting and welding. The paper is based by experiments using YAG:Nd pulse laser (KVANT 17-CIS made). Technological modules were assembled for laser beam deviation and for relative s...
Physical-Mechanical and Technological Characteristics of Ti10Zr Alloy for Dental Applications
Progress reported over time in dentistry can be attributed largely to the dynamics of acquiring new materials. A biomaterial is considered ideal in the absence of any biomaterial-tissue interaction, which means a biomate...
PhysicoMechanical and Physico-Chemical Properties of Bio-Inert Composite Ceramics
Bio-inert ceramics are non-toxic, non-allergenic and non-carcinogenic materials which explain why these are frequently used as orthopedic and dental implants. Unfortunately, these are chemically inert and do not naturall...
Research on the Behaviour of the Tooth - Crown Assemblies Made of Different Metal Materials in Solutions Simulating the Oral Environment
One of the basic principles of restorative dentistry is the conservation of the hard dental structure, while satisfying both aesthetic and functional requirements. Complying with this principle will minimize the harmful...
Aspects Regarding the Widia Plates Behaviour Covered With Tin During the Cutting Process
The microscopic property that depends on the interfacial structure and on the tension to which the interface is submitted is called adherence. The strong connection in the interfacial area, low tension gradients, the abs...