Evaluation of mechanical properties of poly (methyl methacrylate) reinforced with glass fibers
Journal Title: Prosthodontics - Year 2018, Vol 68, Issue 1
Abstract
Introduction. Acrylic resin is a basic material used in preparation of partial and complete dentures. One of the methods of improving mechanical properties of removable dentures is reinforcing acrylic resin with artificial fibers. Aim of the study. To compare mechanical properties of acrylic material reinforced with various types of glass fibers. Material and method. Heat-cured Estetic acrylic resin by Wiedent was used for denture bases. Glass mat, fiberglass fabric, long glass fibers and short glass fibers were used as reinforcing phase of the acrylic resin. In total, forty specimens were prepared, of which eight samples were controls. Research samples consisted of four groups of eight specimens each. Mechanical examinations in three-point bending test were conducted by means of the Zwick 1435 universal testing machine. Results. Specimens reinforced with short glass fibers achieved the highest values of maximum bending force (105.7 ± 8.9 N). It corresponded to the highest values of bending strength (126.8 ± 10.7 MPa). The lowest strength was found for specimens reinforced with glass mat (82.8 ± 11.8 MPa). The highest value of Young’s modulus was obtained for the samples reinforced with fiberglass fabric (3.7 ± 0.8 GPa). The highest values of deflection at maximum bending force were found for the samples reinforced with long glass fibers (4.0 ± 0.6 mm). Conclusions. The highest bending strength parameters were found for specimens reinforced with short and long glass fibers. Short glass fibers are better at improving mechanical properties of acrylic resin than long glass fibers.<br/><br/>
Authors and Affiliations
Bartosz Bienias, Wojciech Michalski, Krzysztof Pietryga, Elżbieta Pamuła, Marek Wasek
Keywords
Related Articles
- EP ID EP273116
- DOI 10.5604/01.3001.0011.6803
- Views 84
- Downloads 0
Long-term clinical observation of overdenture supported by the double crown with clearance fit. A case report
Telescopic prostheses are a useful solution for patients with residual dentition. They ensure good loading of abutment teeth and stability of denture during mastication. In this article the case of a patient using a tele...
Wpływ procedury polimeryzacji na stopień szczelności brzeżnej wypełnień z materiałów złożonych – badania in vitro
Wprowadzenie. Materiały złożone stosuje się obecnie najczęściej w celu rekonstrukcji tkanek zęba. Materiały te kurczą się jednak w czasie polimeryzacji, co powoduje tworzenie się szczeliny brzeżnej między wypełnieniem a...
Porównanie wytrzymałości zębów przednich odbudowanych koronami kosmetycznymi z różnych materiałów
Cel pracy. Celem pracy było porównanie wytrzymałości zębów przednich odbudowanych koronami wykonanymi z dwutlenku cyrkonu, ceramiki leucytowej, kompozytu i akrylu.Materiał i metody. Badanie przeprowadzono metodą elementó...
Zastosowanie wycisku cyfrowego podczas wykonania szyny okluzyjnej, w przypadkach ograniczonego odwodzenia żuchwy
Ograniczenie zakresu odwodzenia żuchwy jest jednym z podstawowych symptomów dysfunkcji narządu żucia. Może ono wystąpić na skutek patologii mięśniowej lub przestrzennych zmian w stawach skroniowo-żuchwowych. Zaniechanie...
Porównanie metod polimeryzacji protez całkowitych – na podstawie piśmiennictwa
Żywica akrylowa wykazuje skurcz polimeryzacyjny powstający podczas przekształcania cząsteczek monomeru w cząsteczki polimeru. Wpływa on na zmianę wymiarów wykonywanej protezy całkowitej prowadząc czasami do nieodpowiedni...