Influence of refining process on the porosity of high pressure die casting alloy Al-Si
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2
Abstract
This study presents research results of the influence that refining and transfer of AlSi12S alloy on the porosity of high pressure diecastings. Tests were conducted under production conditions of Die-casting Foundry META-ZEL Sp z o.o. The operation of refining was conducted in a melting furnace, with the use of an FDU Mini Degasser. Decay of the refining effect was assessed by evaluating the porosity content and metallographic examination.
Authors and Affiliations
A. W. Orłowicz, M. Mróz, J. Betlej, F. Płoszaj
Keywords
Related Articles
- EP ID EP71704
- DOI -
- Views 107
- Downloads 0
Unconventional methods of reclamation of used moulding sands
Analysis of the literature provides information on a constant search for new ways of regenerating of moulding sand deprived disadvantages of existing solutions, especially in the case of low efficiency of regeneration of...
The influence of amperage of electric arc on microhardness in the area single and overlapping remeltings of HS 6-5-2 steel
The present thesis depicts the microhardness of HV0,065 surface layer of high speed steel HS6-5-2 remelted with the electric arc. There were different surface layer variants of remelting used – the amperage was changed f...
Interactions at the mould – modifying coating – molten nickel alloy interface
The study describes thermal-chemical interactions that take place in the molten nickel alloy-ceramic mould system, where the mould is either coated with a modifying coating („blue” mould) or is not („white” mould). The c...
Possibilities of improving the durability of pressure moulds
Possibilities of improving the durability of pressure moulds
Acquisition of technology knowledge from online information sources
The article discusses problems related with the search of information from open sources, particularly on the Internet. Specific area of concern is searching for technical knowledge in the area of metalcasting. The result...