Interaction of sub-zero treated Cr-V ledeburitic steel with alumina,100 Cr6 steel and bronze in dry sliding
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2014, Vol 21, Issue 2
Abstract
The interaction of the Vanadis 6 steel, processed without/with an application of sub-zero treatment, with alumina (hard counterface), 100Cr6-ball bearing steel (counterface of an intermediate hardness) and CuSn6 (soft counterface) has been examined. Obtained results infer that the wear performance against alumina is the best for no-SZT material quenched from higher austenitizing temperature (highest hardness). In dry sliding against 100 Cr6 ball bearing steel, the best wear resistance has been achieved for the material after SZT at -196 oC/10 h. The interaction of Vanadis 6 steel with CuSn6 results in a considerable counterpart material transfer to the samples of Vanadis 6-steel whereas the extent of the transfer is rather independent on both the austenitizing temperature and the SZT parameters, within the range of parameters used for the investigations.
Authors and Affiliations
Peter Jurci, Pavel Bilek, Jana Ptacinova
Keywords
Related Articles
- EP ID EP137615
- DOI -
- Views 115
- Downloads 0
QUANTITATIVE METALOGRAPHY OF HEAT TREATED ŽS6K SUPERALLOY
Alloy ŽS6K is former USSR superalloy used in DV – 2 jet engine. It is used for turbine rotor blade and whole cast small sized rotors with working temperature up to 800 ÷ 1050°C. This alloy was evaluated after annealing a...
THE EFFECT OF THE ANNEALING TEMPERATURE ON THE CORROSION RESISTANCE OF WELD JOINT OF AISI 310 STEEL - SHORT COMMUNICATION
The article presents samples of weld joint of AISI 310 austenitic steel which were subjected to solution annealing at various temperature - time exposures. The objective of the experiment was to determine the annealin...
The influence of heat treatment on properties of lead-free solders
The article is focused on the analysis of degradation of properties of two eutectic lead-free solders SnCu0.7 and SnAg3.5Cu0.7. The microstructures of the intermetallic compound (IMC) layers at the copper substrate - sol...
[i][/i][sub][/sub]MICROSTRUCTURE OF BORONIZED PM Cr-V COLD WORK LEDEBURITIC TOOL STEEL
The PM Vanadis 6 cold work tool steel has been boronized at various processing parameters, austenitized, quenched and tempered to a core hardness of 700 HV. Microstructure, phase constitution and microhardness of boroniz...