The influence of heat treatment on properties of lead-free solders 

Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2015, Vol 22, Issue 1

Abstract

The article is focused on the analysis of degradation of properties of two eutectic lead-free solders SnCu0.7 and SnAg3.5Cu0.7. The microstructures of the intermetallic compound (IMC) layers at the copper substrate - solder interface were examined before and after heat treatment at 150°C for 50, 200, 500 and 1000 hours. The thickness of IMC layers of the Cu6Sn5 phase was growing with the increasing time of annealing and shown the typical scallops. For the heat treatment times of 200 hours and longer, the Cu3Sn IMC layers located near the Cu substrate were also observed. The experiments showed there is a link between the thickness of IMC layers and decrease of the shear strength of solder joints. In general, the joints made of the ternary solder showed higher shear strength before and after heat treatment in comparison to joints from solder SnCu0.7. 

Authors and Affiliations

Lydia Rizekova, Marian Drienovsky, Katarina Pociskova, Milan Ozvold

Keywords

Related Articles

Influence of process parameters on torsional strength, impact toughness and hardness of dissimilar AISI 304 and AISI 1021 friction welded steels 

In this present study an attempt was made to join austenitic stainless steel (AISI 304) with low alloy steel (AISI 1021) at different rotational speeds and at different axial pressures and then determining the strength o...

Optimal welding technology of high strength steel S690QL 

In this paper is presented the detailed procedure for defining the optimal technology for welding the structures made of the high strength steel S690QL. That steel belongs into a group of steels with exceptional mechanic...

 EFFECTIVNESS OF THE FATIGUE CRITERIA FOR COMBINED BENDING – TORSION LOADING

Most of mechanical components in the engineering are frequently subjected to combined loading, which can lead to sudden fatigue failure. In present work the fatigue life of plasma-nitrided and virgin specimens is studied...

Prediction of maximum casting defect size in MAR-M-247 alloy processed by hot isostatic pressing 

Nickel based MAR-M-247 superalloy treated by hot isostatic pressing was investigated with the aim to identify the influence of casting defect size on fatigue life. Two testing temperatures of 650 and 800°C and one stress...

PROTECTIVE LAYERS OF IRON AND NICKEL ALUMINIDES ON STEEL 

Intermediary phases Ni-Al and Fe-Al are promising materials due to their superior properties such as hardness and good resistance against oxidation at high temperatures. Moreover, Fe-Al phases are resistant in sulphur -...

Download PDF file
  • EP ID EP142798
  • DOI -
  • Views 105
  • Downloads 0

How To Cite

Lydia Rizekova, Marian Drienovsky, Katarina Pociskova, Milan Ozvold (2015). The influence of heat treatment on properties of lead-free solders . Materials Engineering - Materialove inzinierstvo (MEMI), 22(1), 1-7. https://europub.co.uk/articles/-A-142798