MODIFICATION OF THE SURFACE LAYER OF SINTERED DUPLEX STAINLESS STEELS THROUGH ALLOYING USING THE GTAW METHOD
Journal Title: Tribologia - Year 2018, Vol 278, Issue 2
Abstract
The demand for materials obtained using powder metallurgy (PM) is constantly increasing, especially on SDSSs, which are characterized by a two–phase structure consisting of ferrite and austenite. The main purpose of this study was to examine the effect of surface layer alloying with chromium carbide on the microstructure and tribological properties (e.g., hardness and wear resistance) of SDSSs. The multiphase sinters were prepared from two types of water–atomized steel powders: 316L and 409L. The technique of the APS method was used to deposit Cr3C2–NiAl powder on the SDSS surface. Electric arc (GTAW method) was used for surface alloying. Optical and scanning microscopy, X–ray phase analysis, and examinations of microhardness and coefficient of friction were performed in order to determine the microstructure and basic properties of SDSS after alloying. The surface alloying with Cr3C2 improves tribological properties of SDSSs such as hardness and the coefficient of friction.<br/><br/>
Authors and Affiliations
Barbara LISIECKA, Agata DUDEK
Keywords
Related Articles
- EP ID EP402705
- DOI 10.5604/01.3001.0012.6979
- Views 76
- Downloads 0
THE EFFECT OF THE DLC LAYER THICKNESS ON THE TRIBOLOGICAL PROPERTIES IN SLIDING FRICTION
This paper presents the results of tribological tests made on the samples with a layer thickness of 50 nm, 500 nm and 1300 nm deposited on the surface of 316L tool steel. The DLC layers were made by the RF PACVD method....
THERMAL, MECHANICAL, AND TRIBOLOGICAL PROPERTIES OF PTFE COMPOSITE WITH 20% GRAPHITE CONTENT IRRADIATED WITH AN ELECTRON BEAM
The paper investigated the effect of irradiation with an electron beam of energy 10MeV in doses of 26-156 kGy on polytetrafluoroethylene with a 20% graphite additive. The tests have shown that changes in thermal properti...
THE INFLUENCE OF CHO ADDITIVES ON THE SURFACE LAYER
The paper presents results of investigations of CHO additives, dissolved in the synthetic oils (PAO4 and Priolube), on the change of composition of the surface layer of the wear scar after the tribological tests under co...
PROCES FORMOWANIA SIĘ WŻERÓW ADHEZYJNYCH W RUCHU OSCYLACYJNYM
Podczas bezpośredniego kontaktu metal–metal zachodzą złożone procesy zużycia tribologicznego. Jednym z najistotniejszych i najbardziej problematycznych zjawisk prowadzących do nieodwracalnych zmian struktury geometryczne...
TESTING OF AN EFFECT OF AUTOMOTIVE AND INDUSTRIAL GEAR OILS ON GEAR MICROPITTING
The aim of the work was to assess the influence of the properties of manual transmission fluids (also called automotive gear oils) on the resistance to micropitting of gears. The FZG GT-C/8,3/90 micropitting test method...