Equi-biaxial loading effect on austenitic stainless steel fatigue life
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 38
Abstract
Fatigue lifetime assessment is essential in the design of structures. Under-estimated predictions may result in unnecessary in service inspections. Conversely, over-estimated predictions may have serious consequences on the integrity of structures. In some nuclear power plant components, the fatigue loading may be equibiaxial because of thermal fatigue. So the potential impact of multiaxial loading on the fatigue life of components is a major concern. Meanwhile, few experimental data are available on austenitic stainless steels. It is essential to improve the fatigue assessment methodologies to take into account the potential equi-biaxial fatigue damage. Hence this requires obtaining experimental data on the considered material with a strain tensor in equibiaxial tension. Two calibration tests (with strain gauges and image correlation) were used to obtain the relationship between the imposed deflection and the radial strain on the FABIME2 specimen. A numerical study has confirmed this relationship. Biaxial fatigue tests are carried out on two austenitic stainless steels for different values of the maximum deflection, and with a load ratio equal to -1. The interpretation of the experimental results requires the use of an appropriate definition of strain equivalent. In nuclear industry, two kinds of definition are used: von Mises and TRESCA strain equivalent. These results have permitted to estimate the impact of the equibiaxiality on the fatigue life of components
Authors and Affiliations
G. Gourdin , S. Bradaï, J. Le Roux , C. Gardin
Keywords
Related Articles
- EP ID EP133760
- DOI 10.3221/IGF-ESIS.38.23
- Views 79
- Downloads 0
Effects of hydrogen induced delay fracture on high-strength steel plate of automobile and the improvement
Delay fracture is an environmental embrittlement occurring when materials, environment and stress interact with each other and also a form of hydrogen induced material deterioration. It is a leading factor inhibi...
Is notch sensitivity a stress analysis problem?
Semi–empirical notch sensitivity factors q have been widely used to properly account for notch effects in fatigue design for a long time. However, the intrinsically empirical nature of this old concept can be avoid...
Estimation of fretting fatigue life using a multiaxial stress-based critical distance methodology
This work presents a methodology for life estimation of mechanical couplings subjected to fretting fatigue. In this approach, a stress-based multiaxial fatigue parameter is evaluated at a critical distance below t...
Evaluation of stress intensity factor of multiple inclined cracks under biaxial loading
A finite rectangular plate of unit thickness with two inclined cracks (parallel and non parallel) under biaxial mixed mode condition are modelled using finite element method. The finite element method is used for d...
Experimental and analytical study of cracks under biaxial fatigue
Most mechanical components experience multi-axial cyclic loading conditions during service. Experimental analysis of fatigue cracks under such conditions is not easy and most works tend to focus more on the s...